In this paper, food packaging materials and bioplastics applied as materials for food packaging are reviewed. Other possible materials, such as plastics, paper, metal, and glass, are also discussed. The advantages and disadvantages of every material are highlighted. The awareness of sustainability and the depletion of petroleum sources have contributed to the studies or innovations of using green materials, such as starch/polylactide, as food packaging. Bioplastic materials have several weaknesses in terms of their mechanical and barrier properties that have resulted in several studies on composite systems. These weaknesses have been reviewed and analyzed to determine the potential of bioplastic composites for application as food packaging materials.

Economic, social, and urban developments generally require improvements in the transportation sector, which includes automobiles such as trucks, buses, trailers, airplanes, and even bicycles. All these vehicles use rubber tires. After consumption, these tires become waste, leading to enlarged landfill areas for used tires and implying additional harm to the environment. This review summarizes the growth of rubber recycling application and the sustainability of using waste rubber in the construction field. Furthermore, we provide methods to convert rubber waste to fuel or fuel additives by using tire-derived fuel and concentrate to pyrolysis, which are environmentally friendly and efficient ways. The related parameters such as temperature, pressure, and feedstock composition were studied. Most research papers observed that 500 °C is the optimal temperature at atmospheric pressure in the presence of a specific type of catalyst to improve pyrolysis rate, oil yield, and quality.

The strong demand for plastic and polymeric materials continues to grow year after year, making these industries critical to address sustainability. By functioning as a filler in either a synthetic or natural starch matrix, nanoclay enables significant reductions in the impact of nonbiodegradable materials. The effect of treated nanoclay (NC) loading on the mechanical and morphological properties (EP) of epoxy is investigated in this research. The NC-EP nanocomposites were prepared via casting. The investigation begins with adding NC at concentrations of 1, 2, and 3 weight percent, followed by the effect of acid treatment on the same nanocomposites. The evaluation is focused on four mechanical tensile strength parameters: Young’s modulus, maximum load, and % elongation. The addition of NC improved the mechanical properties of the four components by 27.2%, 33.38%, 46.98%, and 43.58%, respectively. The acid treatment improved 35.9%, 42.8%, 51.1%, and 83.5%, respectively. These improvements were attributed to NC’s ability to alter the structural morphology as assessed by field emission scanning electron microscopy (FESEM), a tool for analysing the microstructure. FESEM images were used to visualise the interaction between the NC and EP nanocomposites. The dynamic mechanical properties of the hybrid nanocomposites were investigated using storage modulus, loss modulus, and tan(delta). The results have shown that the viscoelastic properties improved as the fraction of NC increased. The overall findings suggest that these nanocomposites could be used in various industrial and biomedical applications.

In this study, a biodegradable, cheap and durable recycled high-density polyethylene (rHDPE) polymer reinforced with rice husk (RH) fibre was fabricated into a foam structure through several processes, including extrusion, internal mixing and hot pressing. The effect of filler loading on the properties of the foam and the influence of RH surface treatments on the filler–matrix adhesion and mechanical properties of the composite foam were investigated. The morphological examination shows that 50 wt.% filler content resulted in an effective dispersion of cells with the smallest cell size (58.3 µm) and the highest density (7.62 × 1011 sel/cm³). This small cell size benefits the mechanical properties. Results indicate that the tensile strength and the Young’s modulus of the alkali-treated RH/rHDPE composite foam are the highest amongst the treatments (10.83 MPa and 858 MPa, respectively), followed by UV/O₃, which has shown considerable increments compared with the untreated composite. The flexural and impact tests also show the increment in strength for the composite foam after chemical treatment. Although the UV/O₃ surface treatment has minor influence on the mechanical enhancement of the composite foam, this method may be a reliable surface treatment of the fibre-reinforced composite.