While most of the influences on the mechanical properties of particleboard appear to have been investigated, there is a lack of knowledge about the influence of particle size or particle dimensions due to the absence of a suitable particle measuring technique. The introduction of laser-based 3D scanning technology makes it possible to automatically determine the dimensions, surface area, and volume of particles. In this study, the influence of particle size on the mechanical properties of particleboards was investigated. To isolate potentially overlapping influences, single-layer particleboards with a uniform density profile were produced and analyzed. The amount of adhesive specific to the surface of the (fine) face layer particles and (coarse) core layer particles was adjusted utilizing 3D scanning of the surface areas to ensure comparability despite changes in particle size. It was found that with increasing particle size, the modulus of rupture (MOR) and modulus of elasticity (MOE) increase, while the internal bond strength (IB) decreases. It is considered whether these effects result from a particle-size-dependent orientation of the particles in the board. Furthermore, it is shown that all the aforementioned properties increase with increasing surface-specific adhesive amounts. Examples are provided to demonstrate how such fundamental relationships can be utilized to enhance the particleboard production process.

Defibration conditions influence wood fiber characteristics and thereby properties of fiber-based materials. In this study, the effects of several defibration conditions on mechanical and physical properties of fiber-based wood-plastic composites (WPCs) are illustrated. Various WPCs were tested containing different thermo-mechanical pulps (TMPs) or groundwood pulp (GWP), whereby material composition (50 wt% wood fibers, 47 wt% polymer, 3 wt% coupling agent) and the production process (internal mixer, injection molder) were kept consistent. The data from the experiment revealed that differing defibration conditions led to statistically significant differences in the tested flexural, tensile, and impact properties as well as in the water absorption of WPC. Overall, the GWP and the TMP which was produced under the mildest defibration conditions performed best in fiber-based WPCs. Therefore, grinders and refiners may be equally suitable to produce pulp for WPC usage. As a side-effect within this study, the reinforcing effect of fiber application on flexural and tensile properties was on an extraordinarily high level.