The investment casting process is widely used in the aerospace industry to produce complex engine parts. The article determines the properties of quartz powders, nanosilica dioxide binders, and multilayer samples of ceramic casting molds. The properties of spherical molds obtained using an alcohol-water system derived from hydrolyzed ethyl silicate (ZKE) and LUDOX PX-30 (type Q1) were compared with those obtained in water systems derived from Remasol Plus and Remasol Premium binders (type Q2). The spherical samples are composed of seven layers made with the use of an immersion-sprinkling method. To assess the properties of the molds, X-ray microscopy (µCT), scanning electron microscopy (SEM), and gas permeability analysis over a temperature range of 20–950 °C were utilized. The binder type is proven to affect the properties of the casting mold samples. The material obtained in the water system, Q2, has advantageous properties such as a high porosity and gas permeability.

In this study, the microstructure and corrosion resistance of the as-extruded and as-extruded with subsequent heat treatment Mg-3Al-1Zn-15Li (LAZ1531) alloys have been investigated. The alloys’ microstructures consisted ofα(Mg),β(Li), Θ-MgLi₂Al and Mg₁₇Al₁₂. As a result of annealing, theβ(Li) toα(Mg) transformation occurred, and the recrystallization supported the reformation of the Mg₁₇Al₁₂. The electrochemical tests showed that the increased amount ofα(Mg) and higher amount of Mg₁₇Al₁₂in the heat-treated alloy favored reactions and determined it as having better corrosion resistance in 3.5 wt.% NaCl.

Two model aluminium-magnesium alloys, containing 3 and 7.5 wt.% of Mg, were subjected to plastic deformation by means of hydrostatic extrusion (HE). Two degrees of deformation were imposed by two subsequent reductions of the diameter. Microstructural analysis and tensile tests of the materials in the initial state and after deformation were performed. For both materials, HE extrusion resulted in the deformation of the microstructure—formation of the un-equilibrium grain boundaries and partition of the grains. What is more, HE resulted in a significant increase of tensile strength and decrease of the elongation, mostly after the first degree of deformation.

Do Muzeum Okręgowego im. Stanisława Staszica w Pile w 2003 r. została przekazana siekierka z piętką typu nordyjskiego. Siekierki tego typu nie występują na terenie Polski. Stan zachowania przedmiotu, charakteryzujący się licznymi uszkodzeniami, mógł być związany z miejscem jego pozyskania (skup metalu). Niedokładny sposób wykonania ornamentu może wskazywać, że siekierka nie jest oryginalnym zabytkiem archeologicznym, ale współczesną kopią. Przeprowadzono analizy traseologiczne oraz analizy składu pierwiastkowego (XRF), które wykazały obecność niedoskonałości produkcyjnych oraz nietypowy dla epoki brązu skład chemiczny wykorzystanego stopu odlewniczego. Pozyskane wyniki pozwalają stwierdzić, że przekazany do muzeum przedmiot to replika siekierki typowej dla terenów Danii i Szwecji. Skłaniają również do refleksji nad występowaniem replik zabytków archeologicznych w zbiorach muzealnych.