Due to an ever-increasing amount of the population focusing more on their personal health, thanks to rising living standards, there is a pressing need to improve personal healthcare devices. These devices presently require laborious, time-consuming, and convoluted procedures that heavily rely on cumbersome equipment, causing discomfort and pain for the patients during invasive methods such as sample-gathering, blood sampling, and other traditional benchtop techniques. The solution lies in the development of new flexible sensors with temperature, humidity, strain, pressure, and sweat detection and monitoring capabilities, mimicking some of the sensory capabilities of the skin. In this review, a comprehensive presentation of the themes regarding flexible sensors, chosen materials, manufacturing processes, and trends was made. It was concluded that carbon-based composite materials, along with graphene and its derivates, have garnered significant interest due to their electromechanical stability, extraordinary electrical conductivity, high specific surface area, variety, and relatively low cost.

Poly(vinylidene fluoride) (PVDF) and its main copolymers - poly(vinylidene fluoride-co-hexafluoropropene), P(VDF-HFP), and poly(vinylidene fluoride-co-trifluoroethylene), P(VDF-TrFE) - were processed by solvent casting at room temperature in the form of porous membranes. Copolymer membranes showed higher degree of porosity than PVDF, the average pore size being larger for P(VDF-TrFE) than for P(VDF-HFP) and PVDF. All membranes show high hydrophobicity with water contact angles in the range 94° to 115°, and electroactive beta phase contents above 90%. The adhesion and proliferation of both C2C12 myoblast and MC3T3-E1 pre-osteoblast cells on the membranes were investigated. It is demonstrated that PVDF membranes promote higher cell proliferation while P(VDF-HFP) membranes show the lowest proliferation for both kinds of cell. The proliferation on P(VDF-TrFE) membranes is cell dependent, higher for MC3T3-E1 cells but lower for C2C12 cells, related to the effect of the highly porous structure on the preferred morphology of each cell type, as the higher pore size and porosity of the P(VDF-TrFE) membrane induce cell elongation, which is preferred just by the C2C12 muscle cells