This study focuses on evaluating the effect of the fineness of basaltic volcanic ash (VA) on the engineering properties of cement pozzolan mixtures. In this study, VA of two different fineness, i.e., VA fine (VF) and VA ultra-fine (VUF) and commercially available fly ash (FA) was used to partially replace cement. Including a control and a hybrid mix (10% each of VUF and FA), eleven mortar mixes were prepared with various percentages of VA and FA (10%, 20% and 30%) to partially replace cement. First, material characterization was performed by using X-ray florescence (XRF), X-ray powder diffraction (XRD), particle size analysis, and a modified Chappelle test. Then, the compressive strength development, alkali silica reactivity (ASR), and drying shrinkage of all mortar mixes were investigated. Finally, XRD analysis on paste samples of all mixes was performed to assess their pozzolanic reactivity at ages of 7 and 91 days. The results showed increased Chappelle reactivity values with an increase in the fineness of the VA. Mortars containing high percentages of VUF (20% and 30%) showed almost equal compressive strength compared to corresponding FA mortars at all ages, however, the hybrid mix (10% VUF + 10% FA) exhibited higher strength than that of the reference mix (100% cement), particularly, at 91 days. At low percentages (10%), ASR expansion in both VF and VUF mortars was higher compared to the corresponding FA mortar and the opposite behavior was observed at high percentages (20% and 30%). Among all the mixes including the control, mortar with VUF was found to be most effective in controlling drying shrinkages at all ages. The rate of consumption of calcium hydroxide (Ca(OH)₂) for pastes containing VUF and FA was almost the same, while VF showed low Ca(OH)₂ intensity. These results indicate that an increase in the fineness of VA significantly improvs performance, and therefore, it could be a feasible substitute for commercial admixtures in cement composites.

The mechanical behavior of basaltic volcanic ash (VA) and fly ash (FA) as a cement replacement under elevated temperatures is mainly investigated in the current study. For this, cement content has been partially replaced with and without the presence of electric arc furnace slag (S). Four distinct ranges of temperatures (200°C, 400°C, 600°C, and 800°C) were selected, and the modified mixes were subjected to these gradually elevated temperatures. Samples were cured and cooled by using air‐ and water‐cooling techniques. Test results were established by examining the sample weights and compressive strength before and after the exposure of each temperature level. The pozzolanic potential of volcanic ash and fly ash samples was identified using the strength activity index. After analyzing the test results, it has been found that there is a significant effect on the compressive strength of mortar mixes at the early ages of its strength gain. However, at the later ages of curing, samples modified with volcanic and fly ash with the presence of electric arc furnace slag have shown a better performance than control mix in terms of strength and weight loss.

In the current research work, an attempt is made to increase the seismic capacity of unreinforced masonry (URM) structures by proposing a new composite material which can improve shear strength and deformation capacity of URM wall systems. Fiber Reinforced Polymer (FRP) having high tensile and shear stiffness can significantly increase in-plane and out-of-plane strength of masonry walls, but, inherently, FRP strengthened wall systems exhibit brittle failure under extreme seismic loading. Polypropylene (PP-band) is a low cost material with sufficient ductility and deformation capacity. Keeping in view the behavior of FRP and PP-band, a composite of FRP and PP-band is proposed for retrofitting of URM walls. Mechanical behavior of the proposed composite material is assessed by carrying out an in-plane diagonal compression test and an out-of-plane bending test on twenty-five 1/4-scaled masonry wall panels. Experimental plan for each panel, URM, PP-band retrofitted, FRP retrofitted and FRP + PP-band retrofitted masonry, is diagonal compression test and three-point bending test. Experimental results have determined that FRP + PP-band composite increased, not only the initial peak strength, but also the ductility, deformation capacity and residual strength of URM wall systems.

In this study, the researchers investigated the potential use of locally available waste materials from the lime stone quarry and the granite industry as a partial replacement of cement. Quarry sites and granite industry in the eastern province of Saudi Arabia produces tons of powder wastes in the form of quarry dust (QD) and granite sludge (GS), respectively, causing serious environmental problems along with frequent dust storms in the area. According to ASTM C109, identical 50-mm3 specimens were cast throughout this study to evaluate the compressive strength development of mortars (7, 28 and 91 days) containing these waste materials. Experimental variables included different percentage replacement of cement with waste materials (GS, QD), fineness of GS, various curing temperatures (20, 40 and 60 °C as local normal and hot environmental temperatures) and curing moisture (continuously moist and partially moist followed by air curing). Finally, the results of mortar containing waste materials were compared to corresponding results of control mortar (CM) and mortar containing fly ash (FA). The test results indicated that under normal curing (20 °C, moist cured), the compressive strength of mortar containing the different percentage of waste materials (QD, GS, FA and their combinations) remained lower than that of CM at all ages. However, the compressive strength of mortar containing waste materials slightly increased with increased fineness of GS and significantly increased under high curing temperatures. It was recommended that more fineness of GS be achieved to use its high percentage replacement with cement (30% or more) incorporating local environmental conditions.

The bending and shear behavior of RC beams strengthened with Carbon Fiber-Reinforced Polymers (CFRP) is the primary objective of this paper, which is focused on the failure mechanisms and on the moment-curvature response prior-to, and post, strengthening with different amounts and layouts of the CFRP reinforcement. Seven reinforced concrete beams were tested in 4-point bending, one without any CFRP reinforcement (control beam, Specimen C1), four with the same amount of CFRP in flexure but with different layouts of the reinforcement for shear (Specimens B1–B4), and two with extra reinforcement in bending, with and without reinforcement in shear (Specimens B6 and B5, respectively). During each test, the load and the mid-span deflection were monitored, as well as the crack pattern. The experimental results indicate that: (a) increasing the CFRP reinforcement above certain levels does not necessarily increase the bearing capacity; (b) the structural performance can be optimized through an appropriate combination of CFRP flexural and shear reinforcement; and (c) bond properties at the concrete–CFRP interface play a vital role, as the failure is very often triggered by the debonding of the CFRP strips. The experimental values were also verified analytically and a close agreement between the analytical and experimental values was achieved.