Background: This study evaluated the marginal adaptation, solubility and biocompatibility of TheraCal LC compared with mineral trioxide aggregate (MTA-Angelus) and Biodentine when used as a furcation perforation repair material. Methods: The marginal adaptation was assessed by scanning electronic microscope and presence of any gap between the dentin surface and filling material in each quadrant of the sample was analyzed at 1000 X magnification. The solubility was measured after one week by the ISO standard method. Biocompatibility was evaluated by the inflammatory response and radiography after one month and three months of repair of experimental furcation perforations in dog's teeth. Results: There were significant differences in the marginal adaptation, solubility and biocompatibility of the tested materials (P < 0.05). TheraCal LC showed the highest frequency distribution of gap presence that was followed by the MTA-Angelus then Biodentine. The least soluble material after one week was TheraCal LC that was followed by the MTA-Angelus and Biodentine. After one month and three months, TheraCal LC showed the highest inflammatory response and highest frequency distribution of radiolucency that was followed by the Biodentine then MTA-Angelus. Conclusion: Unlike Biodentine, TheraCal LC is incapable of alternating the MTA in furcation perforation repair due to its poor biocompatibility and poor marginal adaptation.

This study evaluates clinically the effect of propolis paste on healing of cutaneous wound in dogs. Under general anesthesia and complete aseptic conditions, two full thickness skin wounds (3 cm diameter) were created in each side of the chest in five dogs, one dorsal and one ventral, with 10 cm between them. These wounds were randomly allocated into two groups, control group (10 wounds) and propolis group (10 wounds). Both groups were represented in each dog. The wounds were cleaned with normal saline solution and dressed with macrogol ointment in control group and propolis paste in propolis group, twice daily till complete wound healing. Measurement of the wound area (cm²) was monitored planimetrically at 0, 7, 14, 21, 28, and 35 days after injury. The data were analyzed statistically. The results revealed a significant reduction in the wound surface area in the propolis group after 14 and 21 days compared to control group. The wound reepithelization, contraction, and total wound healing were faster in propolis group than in control group during five weeks of study. In conclusion, propolis paste has a positive impact on cutaneous wound healing and it may be suggested for treating various types of wounds in animals.

This study evaluated the antibacterial efficiency and ability of propolis to promote regeneration of immature permanent non-vital dogs’ teeth. Ninety six immature permanent premolars teeth in 6 mongrel dogs were divided randomly into: experimental teeth (N = 72) and control teeth (N = 24). Periapical pathosis was induced in all experimental and positive control teeth. Experimental teeth were classified according to the used intra-canal medication into: group I (N = 36), propolis paste was used and group II (N = 36), triple antibiotic paste (TAP) was used. Bacteriologic samplings were collected before and after exposure to intra-canal medicaments. After the disinfection period (3 weeks), revascularization was induced in all experimental teeth. Each group was subdivided according to the root canal orifice plug into: subgroup A (N = 18), propolis paste was used and subgroup B (N = 18), mineral trioxide aggregates (MTA) was used. Each subgroup was further subdivided according to the evaluation period into 3 subdivisions (6 teeth each): subdivision 1; after 2 weeks, subdivision 2; after one month and subdivision 3; after 2 months. Positive control group had 12 teeth with induced untreated periapical pathosis. Negative control group had 12 untouched sound teeth. All teeth were evaluated with radiography and histology. The bacteriologic and radiographic data were analyzed using repeated measures ANOVA and post-hoc Tukey tests. The histologic data were analyzed using Kruskal-Wallis test, Mann-Whitney U test with Bonferroni’s adjustment and Chi-square test. The significance level was set at P ≤ .05. There was no significant difference in the antibacterial effectiveness between TAP and propolis groups (P > .05). In all subdivisions, there was no significant difference between the experimental groups in terms of increase in root length and dentin thickness, decrease in apical closure, new hard tissue formation, vital tissue formation inside the pulp canal and apical closure scores (P > .05). Propolis can be comparable with TAP as a disinfection treatment option in regenerative endodontic. As a root canal orifice plug after revascularization of necrotic immature permanent teeth in dogs, propolis induces a progressive increase in root length and dentin thickness and a decrease in apical diameter similar to those of MTA.

This study compared biointeractivity (pH of soaking water and calcium ions), porosity, water sorption, solubility, compressive strength, lap shear strength, as well as the apatite forming ability of three calcium silicate-based capping materials: Mineral trioxide aggregate (MTA), Biodentine (BD) and Tech Biosealer capping (BS). One hundred and five discs of the tested materials were prepared in compliance with the manufacturer’s instructions. The materials' pastes were placed in Teflon molds and allowed to set before testing. The pH and Ca+2 ions were measured by a potentiometric method. Porosity, water sorption, and solubility were calculated through the measurement of initial mass, mass, saturated mass and dry mass. Apatite forming ability was measured by an Environmental Scanning Electron Microscope that was connected to a secondary electron detector for energy dispersive X-ray analysis. Meanwhile compressive strength was measured by a computer controlled universal testing machine. Lap shear strength was measured by computer software on the testing machine. All data were statistically analyzed. The tested materials showed Ca ions release and alkalization, which decreased with soaking time. The BD exhibited a very high Ca release at both short (3 h) and long times (28 days). Significant high values of open and apparent porosities, water sorption, and solubility were measured for BS, which was followed by the MTA then BD (P < .05). The BD had significant higher compressive and lap shear bond strength than the MTA and BS (P < .05). MTA, BD and BS are biointeractive bioactive materials that possess the ability to release ions and form calcium phosphate deposits. Unlike BD, BS is incapable of alternating MTA in pulp capping due to its high porosities, water sorption and solubility, as well as poor compressive and lap shear bond strength.