The extraction yield, phenolic content, anthocyanin content and antioxidant activity of extracts from different varieties of red grapes, Cabernet Sauvignon, Merlot, Petit Verdot, Syrah, Tempranillo and Tintilla, using pressurized green solvents have been analyzed. Two techniques were studied and compared: supercritical fluid extraction (SFE) with CO₂ + 20% ethanol and pressurized liquid extraction (PLE) with either ethanol, water or an ethanol/water mixture as the extraction solvents. The Petit Verdot variety allowed the highest global and phenolic yield, and antioxidant activity. The best conditios for PLE obtained from the experimental design and kinetic study were 50% ethanol/water as the pressurized solvent at 90 bar, 120 °C, a flow rate of 5 g/min and, an extraction time of 90 min. A statistical analysis of variance has been performed and it was found that temperature is the only variable that has a statistical influence on the extraction yield. The antioxidant activity levels of the extracts are very promising and they are similar to those obtained with the antioxidant tocopherol.

There is an increasing demand for the use of new food packaging materials. In this study, natural jute fibers impregnated with a Petit Verdot Red Grape Pomace Extract (RGPE) was proposed as a new active food packaging material. Pressurized Liquid Extraction (PLE) and Enhanced Solvent Extraction (ESE) techniques were employed to obtain the bioactive RGPE. Afterward the supercritical solvent impregnation conditions to obtain RGPE-natural jute fibers were studied, by varying pressure, modifier percentage and dried RGPE mass. PLE technique offered the highest bioactive extract at 20 MPa, 55 °C, 1 h residence time using C₂H₅OH:H₂O (1:1 v/v), providing an EC50 of 3.35 ± 0.25 and antibacterial capacity against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa (MIC of 12.0, 1.5 and 4.0 mg/mL RGPE respectively). The natural jute fibers impregnated with 3 mL of that RGPE (90 mg/mL) at 50 MPa and 55 °C generated the most efficient packing material with regards to its food preservation potential.