Different techniques have been developed to overcome the recalcitrant nature of lignocellulosic biomass and extract lignin biopolymer. Lignin has gained considerable interest owing to its attractive properties. These properties may be more beneficial when including lignin in the preparation of highly desired value-added products, including hydrogels. Lignin biopolymer, as one of the three major components of lignocellulosic biomaterials, has attracted significant interest in the biomedical field due to its biocompatibility, biodegradability, and antioxidant and antimicrobial activities. Its valorization by developing new hydrogels has increased in recent years. Furthermore, lignin-based hydrogels have shown great potential for various biomedical applications, and their copolymerization with other polymers and biopolymers further expands their possibilities. In this regard, lignin-based hydrogels can be synthesized by a variety of methods, including but not limited to interpenetrating polymer networks and polymerization, crosslinking copolymerization, crosslinking grafted lignin and monomers, atom transfer radical polymerization, and reversible addition–fragmentation transfer polymerization. As an example, the crosslinking mechanism of lignin–chitosan–poly(vinyl alcohol) (PVA) hydrogel involves active groups of lignin such as hydroxyl, carboxyl, and sulfonic groups that can form hydrogen bonds (with groups in the chemical structures of chitosan and/or PVA) and ionic bonds (with groups in the chemical structures of chitosan and/or PVA). The aim of this review paper is to provide a comprehensive overview of lignin-based hydrogels and their applications, focusing on the preparation and properties of lignin-based hydrogels and the biomedical applications of these hydrogels. In addition, we explore their potential in wound healing, drug delivery systems, and 3D bioprinting, showcasing the unique properties of lignin-based hydrogels that enable their successful utilization in these areas. Finally, we discuss future trends in the field and draw conclusions based on the findings presented.

Laponite XLS™, which is a synthetic clay of nanometric dimensions containing a peptizing agent, has been associated with silanized hydroxypropylmethylcellulose (Si-HPMC) to form, after crosslinking, a novel composite hydrogel. Different protocols of sample preparation were used, leading to different morphologies. A key result was that the storage modulus of Si-HPMC/XLS composite hydrogel could be increased ten times when compared to that of pure Si-HPMC hydrogel using 2 wt % of Laponite. The viscoelastic properties of the composite formulations indicated that chemical and physical network structures co-existed in the Si-HPMC/XLS composite hydrogel. Images that were obtained from confocal laser scanning microscopy using labelled Laponite XLS in the composite hydrogels show two co-continuous areas: red light area and dark area. The tracking of fluorescent microspheres motions in the composite formulations revealed that the red-light area was a dense structure, whereas the dark area was rather loose without aggregated Laponite. This novel special double-network structure facilitates the composite hydrogel to be an adapted biomaterial for specific tissue engineering. Unfortunately, cytotoxicity’s assays suggested that XLS Laponites are cytotoxic at low concentration. This study validates that the hybrid interpenetrated network IPN hydrogel has a high modulus that has adapted for tissue engineering, but the cell’s internalization of Laponites has to be controlled.

In recent years, multicomponent hydrogels such as interpenetrating polymer networks (IPNs) have emerged as innovative biomaterials due to the synergistic combination of the properties of each network. We hypothesized that an innovative non-animal IPN hydrogel combining self-setting silanized hydroxypropyl methylcellulose (Si-HPMC) with photochemically cross-linkable dextran methacrylate (DexMA) could be a valid alternative to porcine collagen membranes in guided bone regeneration. Calvaria critical-size defects in rabbits were filled with synthetic biphasic calcium phosphate granules in conjunction with Si-HPMC; DexMA; or Si-HPMC/DexMA experimental membranes; and in a control group with a porcine collagen membrane. The synergistic effect obtained by interpenetration of the two polymer networks improved the physicochemical properties, and the gel point under visible light was reached instantaneously. Neutral red staining of murine L929 fibroblasts confirmed the cytocompatibility of the IPN. At 8 weeks, the photo-crosslinked membranes induced a similar degree of mineral deposition in the calvaria defects compared to the positive control, with 30.5 ± 5.2% for the IPN and 34.3 ± 8.2% for the collagen membrane. The barrier effect appeared to be similar in the IPN test group compared with the collagen membrane. In conclusion, this novel, easy-to-handle and apply, photochemically cross-linkable IPN hydrogel is an excellent non-animal alternative to porcine collagen membrane in guided bone regeneration procedures.

Tissue engineering is a multidisciplinary field that relies on the development of customized biomaterial to support cell growth, differentiation and matrix production. Toward that goal, we designed the grafting of silane groups onto the chitosan backbone (Si-chito) for the preparation of in situ setting hydrogels in association with silanized hydroxypropyl methylcellulose (Si-HPMC). Once functionalized, the chitosan was characterized, and the presence of silane groups and its ability to gel were demonstrated by rheology that strongly suggests the presence of silane groups. Throughout physicochemical investigations, the Si-HPMC hydrogels containing Si-chito were found to be stiffer with an injection force unmodified. The presence of chitosan within the hydrogel has demonstrated a higher adhesion of the hydrogel onto the surface of tissues. The results of cell viability assays indicated that there was no cytotoxicity of Si-chito hydrogels in 2D and 3D culture of human SW1353 cells and human adipose stromal cells, respectively. Moreover, Si-chito allows the transplantation of human nasal chondrocytes in the subcutis of nude mice while maintaining their viability and extracellular matrix secretory activity. To conclude, Si-chito mixed with Si-HPMC is an injectable, self-setting and cytocompatible hydrogel able to support the in vitro and in vivo viability and activity of hASC.

Hydrogels are a suitable scaffold material for a variety of tissue engineering applications. However, these materials have a weak structure and require reinforcement. Integrating electrospun fibers could strengthen material properties. This study created fibers and evaluated the influence of the presence of polar head groups within a polysaccharide backbone following functionalization: silated-hydroxypropyl methylcellulose (Si-HPMC). Electrospinning is a multi-parameter, step by step process that requires optimization of solution and process parameters to understand and control the process. Fibers were created for 2%–3% wt/v solutions in water and ethanol. Viscosities of solutions were correlated with spinnability. Variations on process parameters did not reveal major variation on fiber morphology. Once controlled, the process was used for HPMC/Si-HPMC mixture solutions. Solubilization and dilution of Si-HPMC were made with common solvents for electrospinning. Two forms of polymer conformation were electrospun: silanol ending and silanolate ending. Microstructures and resulting nanofibers were analyzed by scanning electron microscopy (SEM) and Energy Dispersive Analysis (EDX). The results show the feasibility of our strategy for creating nanofibers and the influence of polar head groups on electrospinnability.

Three-dimensional (3D) bioprinting has become one of the most advanced and useful innovations that allows the creation of personalized macroscopic and microscopic constructs at different scales that match a patient’s anatomy. Intensive research efforts are currently underway to develop highly printable and biocompatible materials. Among the variety of bioprinting materials (i.e., biomaterial inks), naturally derived hydrogels have attracted great interest due to their beneficial properties in terms of biocompatibility, cost-effectiveness, and biodegradability. In this proceeding paper, we provide an overview of the formulation and use of three functional polysaccharides as ink-based hydrogels. First, 3D bioprinting is summarized as revolutionary technology that is able to create cell-laden structures layer by layer in a specific pattern that mimics native tissue and organs. Cellulose, chitosan, and lignin are presented below, followed by an overview of their applicability in 3D bioprinting, focusing on printability and the resulting printed 3D structures as illustrated in various published figures. In the same way, a comparative overview of 3D bioprinting applications is summarized. Finally, a section dedicated to comparisons, limitations, and crosslinking strategies is provided. It is worth noting that this proceedings paper provides a brief overview rather than a comprehensive review, as it is limited by page constraints and is based on the content of our poster presented at the 1st International Online Conference on Bioengineering.