Novel polymers applied in economic membrane technologies are a perennial hot topic in the fields of natural gas purification and O₂ enrichment. Herein, novel hypercrosslinked polymers (HCPs) incorporating 6FDA-based polyimide (PI) MMMs were prepared via a casting method for enhancing transport of different gases (CO₂, CH₄, O₂, and N₂). Intact HCPs/PI MMMs could be obtained due to good compatibility between the HCPs and PI. Pure gas permeation experiments showed that compared with pure PI film, the addition of HCPs effectively promotes gas transport, increases gas permeability, and maintains ideal selectivity. The permeabilities of HCPs/PI MMMs toward CO₂ and O₂ were as high as 105.85 Barrer and 24.03 Barrer, respectively, and the ideal selectivities of CO₂/CH₄ and O₂/N₂ were 15.67 and 3.00, respectively. Molecular simulations further verified that adding HCPs was beneficial to gas transport. Thus, HCPs have potential utility in fabrication of MMMs for facilitating gas transport in the fields of natural gas purification and O₂ enrichment.

In the production of acrylic acid, the concentration of acrylic acid solution from the adsorption tower was low, which would lead to significant energy consumption in the distillation process to purify acrylic acid, along with the production of a large amount of wastewater. Reverse osmosis (RO) was proposed to concentrate the acrylic acid aqueous solution taken from a specific tray in the absorption tower. The effects of operating conditions on the permeate flux and acid retention were studied with two commercial RO membranes (SWC5 and SWC6). When the operating pressure was 4 MPa and the temperature was 25 °C, the permeate fluxes of two membranes were about 20 L·m⁻²·h⁻¹. The acrylic acid and acetic acid retentions were about 80% and 78%, respectively. After being immersed in the acid solutions for several months, the characteristics of the two membranes were tested to evaluate their acid resistance. After six months of exposure to the acid solution containing 2.5% acrylic acid and 2.5% acetic acid, the retentions of acrylic acid and acetic acid were decreased by 5.7% and 4.1% for SWC5 and 4.9% and 2.2% for SWC6, respectively. The changes of membrane surface morphology and chemical composition showed the hydrolysis of some amide bonds.