A major factor slowing down the establishment of additive manufacturing processes as production processes is insufficient reproducibility and productivity. Therefore, this work investigates the influence of ring-shaped beam profiles on process stability and productivity in laser-based powder bed fusion of AISI 316L. For this purpose, the weld track geometries of single tracks and multi-track segments with varying laser power, scan speed, hatch distance, and beam profile (Gaussian profile and three different ring-shaped profiles) are analyzed. To evaluate the process robustness, process windows are identified by classifying the generated single tracks into different process categories. The influence of the beam profiles on productivity is studied by analyzing the molten cross-sectional areas and volumes per time. When using ring-shaped beam profiles, the process windows are significantly larger (up to a laser power of 1050 W and a scanning speed of 1700 mm/s) than those of Gaussian beams (laser power up to 450 W and scanning speed up to 1100 mm/s), which suggests a higher process robustness and stability. With ring-shaped beam profiles, larger volumes can be stably melted per track and time. The weld tracks created with ring-shaped profiles are significantly wider than those generated with Gaussian profiles (up to factor 2 within the process window), allowing enlargement of the hatch distances. Due to the higher scanning speeds and the enlarged hatch distances for ring-shaped beam profiles, the process can be accelerated by a factor of approximately 2 in the parameter range investigated.

Selective laser sintering (SLS) of thermoplastic materials is an additive manufacturing process that overcomes the boundary between prototype construction and functional components. This technique also meets the requirements of traditional and established production processes. Crystallization behavior is one of the most critical properties during the cooling process and needs to be fully understood. Due to the huge influence of crystallization on the mechanical and thermal properties, it is important to investigate this process more closely. A commercial SLS polyamide (PA12) powder was measured with differential scanning calorimetry (DSC) to model a wider temperature range. To model isothermal crystallization between 160 and 168 °C, the Avrami model was used to determine the degree of crystallization. For non-isothermal crystallization between 0.2 and 20 K/min, different models were compared including the Ozawa, Jeziory, and Nakamura equations.

Additive manufacturing technologies, such as selective laser melting of polymers enable manufacturing of complex parts without tools and forms. Due to high temperature during processing, a degradation of the used plastic powder occurs. The unmolded material in the building chamber, the so-called partcake, can be removed from the finished component after building and reused for another process. To realize reproducible part properties refreshing of partcake powder is necessary. This paper presents results on the investigations of degradation behavior of polyamide 12 powder during selective laser melting process. The influence of different ambient conditions, e.g. ambient air, nitrogen and vacuum, is investigated in a model experiment. Oven aged polymer powders were analyzed with regard to their process relevant material properties. Considered material properties are phase transition temperatures, melting viscosity or molecular weight. The results of the investigations show, that the influence of high process temperatures on used material can be reduced using other ambient conditions. Process relevant material properties are minor affected by storage under vacuum. In addition to that the influence of different ambient conditions as well as a material pretreatment on the degradation behavior of sls materials, e.g. exclusion of intermolecular located oxygen, is analyzed. To correlate these results of the model experiment with real manufacturing process laser sintering experiments are done. PA12 powder is used for several building processes with refreshing. Produced specimens and resulting partcake powder are analyzed and correlated to the results of model experiment. Correlating effects, regarding process relevant material properties as well as aging influenced mechanical properties of specimens can be detected.

Commercially available materials for selective laser sintering (SLS) include mainly semicrystalline polymers and only a few composites like polyamide 12 filled with glass beads or aluminum. Powder composites can be used for setting tailored properties. Exemplarily, mechanical properties as well as thermal or electrical conductivity can be improved. Thermally conductive SLS parts filled with copper particles have not been under investigation before. This study contains the characterization of polyamide 12 filled with copper acting as a metal filler with a high thermal conductivity. Two composites differing in the filler shapes are investigated concerning powder properties and the resulting processability. The thermal conductivity in dependence on the filler content and anisotropy is of major interest. Isotropic, spherically shaped copper fillers are compared with strongly anisotropic flakes leading to the result that a much lower content of anisotropic filler is needed to reach an increased thermal conductivity. However, the powder flowability and processability is also highly influenced by the filler shape and content. Fillers with a similar shape like the matrix powder lead to a better flowability allowing higher filler contents. POLYM. COMPOS., 40:1801–1809, 2019. © 2018 The Authors Polymer Composites published by Wiley Periodicals, Inc. on behalf of Society of Plastics Engineers