Surfactants are used to stabilize nanoemulsions by protecting their physical stability and preventing deterioration of the entrapped bioactive during processing and storage. The effect of surfactant concentration on physical-chemical properties of nanoemulsions with entrapped curcumin, relevant to commercial applications, was addressed in this research. Furthermore, the functionality of nanoemulsified curcumin in terms of lipid oxidation inhibition was determined. Protection against varying pH and thermal treatments was more significant in the nanoemulsions at the elevated surfactant level, but at these high concentrations, the surface charges of the emulsions dramatically decreased under sodium salt addition, which may result in instability over time. Nanoemulsions showed the potential to inhibit malondialdehyde (MDA) formulation by protecting the entrapped curcumin and enhance its antioxidant activity when added to milk. The fortified milk with added curcumin systems had a yellow color compared to the control. The results of the study are critical in choosing the surfactant concentration needed to stabilize emulsified curcumin, and to protect the entrapped curcumin under specific conditions of use to support the utilization of curcumin nanoemulsions as a food additive in different commercial products.

Oil palm empty fruit bunch (EFB) pulp with the highest cellulose content of 83.42% was obtained from an optimized process of acid pretreatment (0.5% v/v H₂SO₄), alkaline extraction (15% w/w NaOH), and hydrogen peroxide bleaching (10% w/v H₂O₂), respectively. The EFB cellulose was carboxymethylated, and the obtained carboxymethyl cellulose (CMC) was readily water-soluble (81.32%). The EFB CMC was blended with glycerol and cast into a composite film. Lignin that precipitated from the EFB black liquor was also incorporated into the film at different concentrations, and its effect on the UV-blocking properties of the film was determined. Interestingly, the EFB CMC film without lignin addition completely blocked UV-B transmittance. The incorporation of lignin at all concentrations significantly enhanced the UV-A blocking and other physical properties of the film, including the surface roughness, thickness, and thermal stability, although the tensile strength and water vapor permeability were not significantly affected. Complete UV-A and UV-B blocking were observed when lignin was added at 0.2% (w/v), and the film also exhibited the highest antioxidant activity against 2,2-diphenyl-1-picrylhydrazyl (DPPH) free radicals with an half-maximal inhibitory concentration (IC₅₀) value of 3.87 mg mL^–1.

In an attempt to find a thermostable xylanase enzyme for potential application in the pretreatment prior to H₂O₂bleaching of paper pulp for industry, an extracellular xylanase fromAureobasidium pullulansCBS 135684 was purified 17.3-fold to apparent homogeneity with a recovery yield of 13.7%. Its molecular mass was approximately 72 kDa as determined by SDS-PAGE. The optimal pH and temperature for activity of the purified enzyme were pH 6.0 and 70°C, respectively. The enzyme was relatively stable at 50°C, retaining more than half of its original activity after 3-h incubation. The thermostability of the enzyme was improved by the addition of 0.75 mM sorbitol prolonging the enzyme’s activity up to 10-fold at 70°C. When the potential of using the enzyme in pretreatment of rice straw pulp prior to bleaching was evaluated, the greatest efficiency was obtained in a mixture containing xylanase and sorbitol. Treatment of the rice straw pulp with xylanase prior to treatment with 10% (v/v) H₂O₂and production of hand sheets increased the ISO sheet brightness by 13.5% and increased the tensile and tear strengths of the pulp by up to 1.16 and 1.71-fold, respectively, compared with pulps treated with H₂O₂alone. The results suggested the potential application of the enzyme before the bleaching process of paper pulp when the maintenance of high temperature and enzyme stability are desirable.