To enhance the properties of polyamide 12 (PA12/Nylon 12) manufactured by the selective laser sintering (SLS) process, micron-sized glass beads are used as a filler, and the resulting composite is known as glass bead-filled PA12 (PA 3200 GF). Despite PA 3200 GF basically being a tribological-grade powder, very little has been reported on the tribological properties of laser-sintered objects based on this powder. As the properties of SLS objects are orientation-dependent, this study is devoted to investigating the friction and wear characteristics of the PA 3200 GF composite sliding against the steel disc in the dry-sliding mode. The test specimens were aligned in the SLS build chamber along five different orientations (X-axis, Y-axis, Z-axis, XY-plane, and YZ-plane). Additionally, the interface temperature and the friction-induced noise were measured. The pin-shaped specimens were examined using a pin-on-disc tribo-tester for 45 min to investigate the steady-state tribological characteristics of the composite material. The results revealed that the orientation of build layers relative to the sliding plane was a ruling parameter that determined the dominant wear pattern and the wear rate. Accordingly, where build layers were parallel or inclined to the sliding plane, abrasive wear predominated, and wear rate became 48% higher than that of specimens with perpendicular build layers, for which adhesive wear predominated. Interestingly, a noticeable synchronous variation of adhesion and friction-induced noise was observed. Taken together, the results from this study can efficiently serve the goals of fabricating SLS-functional parts with customized tribological properties.

Reinforcing thermoplastic materials for additive manufacturing with either short, long, and continuous fibers or micro/nanoparticles is a sound means to enhance the mechanical/tribological properties of functional 3D printed objects. However, despite the fact that reinforced thermoplastics are being used extensively in modern applications, little data are found in open literature regarding the effect of such reinforcements on the friction and wear characteristics of additively manufactured objects. Therefore, this article presents a comparative study that aims to investigate the friction and wear behavior of carbon fiber-reinforced polyamide 12 (CF-PA12) as compared to pure polyamide 12 (PA12). The test specimens were prepared by selective laser sintering (SLS) at five different build orientations and examined using a pin-on-disc tribometer in dry sliding mode. The coefficient of friction (COF), interface temperature, friction-induced noise, and specific wear rate were measured. Scanning electron microscopy (SEM) was used to inspect the tribo-surfaces. The results revealed that both the COF and contact temperature of CF-PA12 are orientation-independent and are lower than those of pure PA12. Also, it was found that, compared with pure PA12, CF-PA12 has 25% smaller COF and 15–40% higher wear resistance. Further, the SEM of tribo-surfaces showed that adhesive wear dominates the surface of pure PA12, while both adhesive and abrasive wear patterns coexist in CF-PA12. Moreover, fiber crushing and thinning were observed, and this, under some circumstances, can result in a considerable increase in frictional noise.

Carbon fiber-reinforced polymers (CFRPs) are being used extensively in modern industries that require a high strength-to-weight ratio, such as aerospace, automotive, motorsport, and sports equipment. However, although reinforcement with carbon fibers improves the mechanical properties of polymers, this comes at the expense of abrasive wear resistance. Therefore, to efficiently utilize CFRPs in dry sliding contacts, solid lubricant is used as a filler. Further, to facilitate the fabrication of objects with complex geometries, selective laser sintering (SLS) can be employed. Accordingly, in the present work, graphite-filled carbon fiber-reinforced polyamide 12 (CFR-PA12) specimens were prepared using the SLS process to explore the dry sliding friction and wear characteristics of the composite. The test specimens were aligned along four different orientations in the build chamber of the SLS machine to determine the orientation-dependent tribological properties. The experiments were conducted using a pin-on-disc tribometer to measure the coefficient of friction (COF), interface temperature, friction-induced noise, and specific wear rate. In addition, scanning electron microscopy (SEM) of tribo-surfaces was conducted to specify the dominant wear pattern. The results indicated that the steady-state COF, contact temperature, and wear pattern of graphite-filled CFR-PA12 are orientation-independent and that the contact temperature is likely to approach an asymptote far below the glass transition temperature of amorphous PA12 zones, thus eliminating the possibility of matrix softening. Additionally, the results showed that the Z-oriented specimen exhibits the lowest level of friction-induced noise along with the highest wear resistance. Moreover, SEM of tribo-surfaces determined that abrasive wear is the dominant wear pattern.

Erosion and erosion–corrosion tests of as-built Ti-6Al-4V manufactured by Selective Laser Melting were investigated using slurries composed of SiO₂ sand particles and either tap water (pure water) or 3.5% NaCl solution (artificial seawater). The microhardness value of selective laser melting (SLM)ed Ti-6Al-4V alloy increased as the impact angle increased. The synergistic effect of corrosion and erosion in seawater is always higher than erosion in pure water at all impact angles. The seawater environment caused the dissolution of vanadium oxide V₂O₅ on the surface of SLMed Ti-6Al-4V alloy due to the presence of Cl⁻ ions in the seawater. These findings show lower microhardness values and high mass losses under the erosion–corrosion test compared to those under the erosion test at all impact angles.