Well-defined linear and multi-arm star polymer structures were used as the templates for in situ synthesis and stabilization of silver nanoparticles (AgNPs). This approach led to hybrid nanomaterials with high stability and antibacterial activity to both Gram-positive and Gram-negative bacterial strains. The ecologically friendly so called “green” synthesis of nanomaterials was performed through AgNPs preparation in the aqueous solutions of star and linear poly(N,N′-dimethylaminoethyl methacrylate)s (PDMAEMAs); the process was followed with time. The size, shape, and zeta potential of the obtained hybrids were determined. To our knowledge, this is the first time that the antibacterial activity of PDMAEMA hybrid nanomaterial against Bacillus subtilis, Escherichia coli and Pseudomonas aeruginosa was investigated and assessed by minimum inhibitory concentration (MIC) and minimum biocidal concentration (MBC). Completely quaternized with ethyl bromide, star and linear PDMAEMAs were used in comparative biological tests. The modification of the polymers with in situ-formed AgNPs increased the antibacterial properties against all studied strains of bacteria by several times in comparison to non-modified polymers and quaternized polymers. These results yield novel nanohybrid materials that can be useful for applications in medicine and biology.

Modern medicine has undoubtedly achieved enormous progress in applying various polymer-based materials for specific applications. Despite this, there is still a need to create systems, especially on the nano-scale, that are simultaneously nontoxic, biocompatible and able to be functionalized with active biomolecules. Polyglycidol (also called polyglycerol) is biocompatible and hydrophilic polymer, that forms different, sometimes complex, polymer architecture, possesses satisfactory stability and has a hydroxyl group on each unit capable for numerous modifications. All of these are undisputed advantages of this polymer. The potential application of this polymer and its derivatives in e.g. macromolecular therapeutics, bioconjugation with peptides, and as drug delivery systems or imaging agents has been examined and described. Nowadays, due to the possibility of using advanced synthetic methodologies, the development of new systems or devices based on polyglycidol is possible for well-defined applications. This review summarizes the results concerning the covalent immobilization of polyglycidol of linear and branched architecture on different 2 D or 3 D supports. A comprehensive overview is provided in relation to the synthetic strategy, properties of polyglycidol layers, its modification and application in reconstructive medicine or tissue engineering as antifouling surfaces, surfaces for cell engineering and imaging or for the immobilization of bioactive compounds.

Poly(2-oxazoline) (POx) matrices in the form of non-woven fibrous mats and three-dimensional moulds were obtained by electrospinning and fused deposition modelling (FDM), respectively. To obtain these materials, poly(2-isopropyl-2-oxazoline) (PiPrOx) and gradient copolymers of 2-isopropyl- with 2-n-propyl-2-oxazoline (P(iPrOx-nPrOx)), with relatively low molar masses and low dispersity values, were processed. The conditions for the electrospinning of POx were optimised for both water and the organic solvent. Also, the FDM conditions for the fabrication of POx multi-layer moulds of cylindrical or cubical shape were optimised. The properties of the POx after electrospinning and extrusion from melt were determined. The molar mass of all (co)poly(2-oxazoline)s did not change after electrospinning. Also, FDM did not influence the molar masses of the (co)polymers; however, the long processing of the material caused degradation and an increase in molar mass dispersity. The thermal properties changed significantly after processing of POx what was monitored by increase in enthalpy of exo- and endothermic peaks in differential scanning calorimetry (DSC) curve. The influence of the processing conditions on the structure and properties of the final material were evaluated having in a mind their potential application as scaffolds.

Polymer nanogels—considered as nanoscale hydrogel particles—are attractive for biological and biomedical applications due to their unique physicochemical flexibility. However, the aggregation or accumulation of nanoparticles in the body or the occurrence of the body’s defense reactions still pose a research challenge. Here, we demonstrate the fabrication of degradable nanogels using thermoresponsive, cytocompatible poly[oligo(ethylene glycol) methacrylate]s-based copolymers (POEGMA). The combination of POEGMA’s beneficial properties (switchable affinity to water, nontoxicity, non-immunogenicity) along with the possibility of nanogel degradation constitute an important approach from a biological point of view. The copolymers of oligo(ethylene glycol) methacrylates were partially modified with short segments of degradable oligo(lactic acid) (OLA) terminated with the acrylate group. Under the influence of temperature, copolymers formed self-assembled nanoparticles, so-called mesoglobules, with sizes of 140–1000 nm. The thermoresponsive behavior of the obtained copolymers and the nanostructure sizes depended on the heating rate and the presence of salts in the aqueous media. The obtained mesoglobules were stabilized by chemical crosslinking via thiol-acrylate Michael addition, leading to nanogels that degraded over time in water, as indicated by the DLS, cryo-TEM, and AFM measurements. Combining these findings with the lack of toxicity of the obtained systems towards human fibroblasts indicates their application potential.