Ammonium thiosulfate is an alternative lixiviant for the hydrometallurgical treatment of sulfide gold ores. The present study is primarily focused on ammonium thiosulfate leaching of gold (Au) and silver (Ag) from the sulfide ore (Sunshin mine in Korea). The main chemical composition of the concentrate was Au (84 ppm), Ag (852 ppm), Fe (18.9%), Si (23.2%), and S (21.1%). The effects of various parameters on the process, such as leaching time (1–4 h), ammonium thiosulfate concentration (0.05–0.5 M), copper sulfate (CuSO₄), concentration (0.05–0.25 M), solid to liquid ratio (0.2–0.5), and reaction temperature (40–60 °C) were systematically examined. Optimum Au leaching efficiency (>99%) was obtained under the following leaching conditions: 0.5 M ammonium thiosulfate with 0.05 M CuSO₄ concentration, 0.2 S/L ratio at 60 °C for 2 h. The results indicate that the behavior of Ag was similar to that of Au. Almost complete dissolution of Ag occurred under following leaching conditions: 0.5 M ammonium thiosulfate with 0.05 M CuSO₄ concentration at 60 °C for 4 h. This study would be useful in understanding the eco-friendly leaching systems of Au and Ag during the hydrometallurgical process of sulfide gold ore.

The removal of the cyanide and copper (Cu) from the waste printed circuit boards (WPCBs) cyanide leach solution through the alkaline chlorination using electro-generated hypochlorite (NaOCl) followed by magnetite (Fe₃O₄) adsorption is investigated. The efficiency of the destruction of cyanide and precipitation of Cu was increased with increasing the concentration of free available chlorine in NaOCl. More than 99% of free cyanide and 76% of Cu were removed under the following conditions: concentration of chlorine in electro-generated NaOCl, 5.2 g/L; volume ratio of NaOCl/leach solution, 1; pH, ~9.8; ambient temperature for 12 h. Then, magnetite adsorption for selective removal of remaining Cu (50.5 mg/L) was selected and more than 99% of copper ion was successfully removed with dosage 10g/100mL, shaking speed 150 rpm within 30 min. The results revealed that the alkaline chlorination using electro-generated NaOCl followed by magnetite adsorption could completely remove the cyanide and Cu, remaining Au in the final solution.