The feasibility of selective laser melting (SLM) was investigated for manufacturing WC-20Co cemented carbide in this study. Both the microstructure analysis and finite element simulation were used to investigate the sintering mechanisms of cemented carbides during SLM process. Characterisation of WC grain size and distribution for SLM processed cemented carbides, as well as the finite element simulation, was conducted. It was shown that during SLM processing, extremely high sintering temperature combined with the short soaking time contributes to the unique inhomogeneous microstructure and densification behaviour of cemented carbide samples. The synergy of laser power and scanning speed determines the maximum sintering temperature during SLM processing.

In-situ synthesis, microstructure, and mechanical properties of four TiB₂-Reinforced Fe-Cr-Mn-Al Steel Matrix Composites have been researched in this work. The microstructure and phases of the prepared specimens have been characterized by using scanning electron microscopy (SEM), X-ray diffraction technique, and transmission electron microscopy (TEM). The sintered specimens consisted of Fe₂AlCr, CrFeB-type boride, and TiB₂. The mechanical properties, such as hardness and compression strength at room temperature (RT) and at elevated temperatures (600 °C and 800 °C) have been evaluated. The compressive strength and Vickers hardness of the sintered specimens increase with the volume fraction of TiB₂ in the matrix, which are all much higher than those of the ex-situ TiB₂/Fe-15Cr-20Mn-8Al composites and the reported TiB₂/Fe-Cr composites with the same volume fraction of TiB₂. The highest Vickers hardness and compressive strength at room temperature are 1213 ± 35 HV and 3500 ± 20 MPa, respectively. As the testing temperature increases to 600 °C, or even 800 °C, these composites still show relatively high compressive strength. Precipitation strengthening of CrFeB and in-situ synthesis of TiB₂ as well as nanocrystalline microstructure produced by the combination of mechanical alloying (MA) and spark plasma sintering (SPS) can account for the high Vickers hardness and compressive strength.