Mixed ionic-electronic conducting membranes have seen significant progress over the last 25 years as efficient ways to obtain oxygen separation from air and for their integration in chemical production systems where pure oxygen in small amounts is needed. Perovskite materials are the most employed materials for membrane preparation. However, they have poor phase stability and are prone to poisoning when subjected to CO₂ and SO₂, which limits their industrial application. To solve this, the so-called dual-phase membranes are attracting greater attention. In this review, recent advances on self-supported and supported oxygen membranes and factors that affect the oxygen permeation and membrane stability are presented. Possible ways for further improvements that can be pursued to increase the oxygen permeation rate are also indicated. Lastly, an overview of the most relevant examples of membrane reactors in which oxygen membranes have been integrated are provided.

Membrane reactors have demonstrated a large potential for the production of hydrogen via reforming of different feedstocks in comparison with other reactor types. However, the long-term performance and stability of the applied membranes are extremely important for the possible industrial exploitation of these reactors. This study investigates the long-term stability of thin-film Pd-Ag membranes supported on porous Al₂O₃ supports. The stability of five similarly prepared membranes have been investigated for 2650 h, up to 600 °C and in fluidized bed conditions. Results show the importance and the contribution of the sealing of the membranes at temperatures up to 500 °C. At higher temperatures the membranes surface deformation results in pinhole formation and a consequent decrease in selectivity. Stable operation of the membranes in a fluidized bed is observed up to 450 °C, however, at higher temperatures the scouring action of the particles under fluidization causes significant deformation of the palladium surface resulting in a decreased selectivity.

The aim of the present work is the recycling treatment of tubular α-Al₂O₃-supported ceramic membranes with a Pd/Ag selective layer, employed in hydrogen production with integrated CO₂ capture. A nitric acid leaching treatment was investigated, and recovered ceramic supports were characterized, demonstrating their suitability for the production of novel efficient membranes. The main objective was the metal dissolution that preserved the support integrity in order to allow the recovered membrane to be suitable for a new deposition of the selective layer. The conditions that obtained a satisfactory dissolution rate of the Pd/Ag layer while avoiding the support to be damaged are as follows: nitric acid 3 M, 60 °C and 3.5 h of reaction time. The efficiency of the recovered supports was determined by nitrogen permeance and surface roughness analysis, and the economic figures were analysed to evaluate the convenience of the regeneration process and the advantage of a recycled membrane over a new membrane. The experimentation carried out demonstrates the proposed process feasibility both in terms of recycling and economic results.