Fluorescence spectroscopy on a series of aqueous solutions of poly(acrylic acid) containing a luminescent label showed that polymers with molar mass, M_n < 16.5 kDa did not exhibit a pH responsive conformational change, which is typical of higher molar mass poly(acrylic acid). Below this molar mass, polymers remained in an extended conformation, regardless of pH. Above this molar mass, a pH-dependent conformational change was observed. Diffusion-ordered nuclear magnetic resonance spectroscopy confirmed that low molar mass polymers did not undergo a conformational transition, although large molar mass polymers did exhibit pH-dependent diffusion.

In this investigation, we report a non-covalent (ionic interlocking and hydrogen bonding) strategy of self-healing in a covalently crosslinked organic–inorganic hybrid nanocomposite hydrogel, with specific emphasis on tuning its properties fitting into a muscle mimetic material. The hydrogel was prepared via an in situ free radical polymerization of sodium acrylate (SA) and successive crosslinking in the presence of starch grafted with poly(2-(methacryloyloxy)ethyl trimethyl ammonium chloride) (PMTAC) and montmorillonite modified with cetyl ammonium bromide (OMMT). This hydrogel shows stimuli triggered self-healing following damage in both neutral and acidic solutions (pH = 7.4 and pH = 1.2). This behavior was reported using stress–strain experiments and rheological analyses of the hydrogel segments joined at their fracture points. The hydrogel was also able to display shape memory properties in the presence of water as well as stimuli (salt, acid and electric impulse) driven actuation behavior. It was observed that the ultimate tensile strength (UTS) of the self-healed hydrogel at pH = 7.4 was comparable to the extensor digitorum longus (EDL) muscle of a New Zealand white rabbit and the as synthesized self-healable hydrogel was found to be non-cytotoxic against NIH 3T3 fibroblast cells.

Interpolymer complex formation of poly(acrylic acid) with other macromolecules can occur via several mechanisms that vary depending on the pH. At low pH the protonated acid functional group can form bonds with both donor and acceptor moieties, resulting in desolvated structures consisting of two polymers. Complexes were formed in dilute solutions of PAA, functionalised with acenaphthylene, with a range of other polymers including: poly(NIPAM); poly(ethylene oxide) (PEO); poly(dimethylacrylamide) (PDMA); poly(diethyl acrylamide) (PDEAM) poly(vinyl alcohol) (PVA) and poly(vinyl pyrolidinone) (PVP). Fluorescence anisotropy was used to demonstrate complex formation in each case by monitoring the reductions in segmental motion of the chain as the complexes formed. Considerations of the molecular structures of the complexing moieties suggest that solvation energies and pK_as play an important role in complex formation.

Highly-branched poly(N-isopropyl acrylamide)s in water pass through coil-to-globule transitions. Using calorimetry and the colour change of a solvatochromic dye within the polymer, we show that some compositions have biphasic core–shell morphologies, with globular cores and open coil shells. The two-phase structure is favoured by increased branching and arises because the chain ends penetrate only to a limited degree into the polymer coil.

The behavior of a linear copolymer of N-isopropylacrylamide with pendant vancomycin functionality was compared to an analogous highly branched copolymer with vancomycin functionality at the chain ends. Highly branched poly(N-isopropylacrylamide) modified with vancomycin (HB-PNIPAM-van) was synthesized by functionalization of the HB-PNIPAM, prepared using reversible addition–fragmentation chain transfer polymerization. Linear PNIPAM with pendant vancomycin functionality (L-PNIPAM-van) was synthesized by functionalization of poly(N-isopropylacrylamide-co-vinyl benzoic acid). HB-PNIPAM-van aggregated S. aureus effectively, whereas the L-PNIPAM-van polymer did not. It was found that when the HB-PNIPAM-van was incubated with S. aureus the resultant phase transition provided an increase in the intensity of fluorescence of a solvatochromic dye, nile red, added to the system. In contrast, a significantly lower increase in fluorescence intensity was obtained when L-PNIPAM-van was incubated with S. aureus. These data showed that the degree of desolvation of HB-PNIPAM-van was much greater than the desolvation of the linear version. Using microcalorimetry, it was shown that there were no significant differences in the affinities of the polymer ligands for d-Ala-d-Ala and therefore differences in the interactions with bacteria were associated with changes in the probability of access of the polymer bound ligands to the d-Ala-d-Ala dipeptide. The data support the hypothesis that generation of polymer systems that respond to cellular targets, for applications such as cell targeting, detection of pathogens etc., requires the use of branched polymers with ligands situated at the chain ends.

Size Exclusion Chromatography is traditionally carried out in either aqueous or non-polar solvents. A system to present molar mass distributions of polymers using methanol as a mobile phase is presented. This is shown to be a suitable system for determining the molar mass distributions poly(N-isopropylacrylamide)s (PNIPAM); a polymer class that is often difficult to analyze by size exclusion chromatography. DOSY NMR was used to provide intrinsic viscosity data that was used in conjunction with a viscometric detector to provide absolute calibration. Then the utility of the system was shown by providing the absolute molar mass distributions of dispersed highly branched PNIPAM with biologically functional end groups.