Selective laser melting (SLM) offers significant potential for the manufacture of the advanced complex-shaped aluminium matrix composites (AMCs) used in the aerospace and automotive domains. Previous studies have indicated that advanced composite powders suitable for SLM include spherical powders with homogeneous reinforcement distribution, a particle size of <100μm and good flowability (Carr index<15%); however, the production of such composite powders continues to be a challenge. Due to the intensive impacts of grinding balls, the high-energy ball-milling (HEBM) process has been employed to refine Al particles and disperse the nano Al2O3 reinforcements in the Al matrix to improve their mechanical properties. Notwithstanding, the specific characteristics of ball-milled powders for SLM and the effect of milling and pause duration on the fabrication of composite powders have not previously been investigated. The aim of this study was to synthesise Al-4vol.% Al2O3 nano-composite powders using HEBM with two different types of milling and pause combinations. The characteristics of the powders subjected to up to 20h of milling were investigated. The short milling (10min) and long pause (15min) combination provided a higher yield (66%) and narrower particle size distribution range than long milling (15min) and a short pause (5min). The nano Al2O3 reinforcements were observed to be dispersed uniformly after 20h of milling, and the measured Carr index of 13.2% indicated that the ball-milled powder offered good flowability. Vickers micro-hardness tests indicated that HEBM significantly improved the mechanical properties of the ball-milled powders

The selective laser melting (SLM) of aluminium alloys is of interest to researchers because of these alloys’ potential applications in the aerospace and automotive domains. Post-processing is generally required in order to enhance the mechanical properties of devices that involve moving parts, where surface mechanical properties are significant factors. This paper describes a preliminary study that was conducted to investigate the effect of post-processing on the microstructure and mechanical properties of SLM fabricated AlSi10Mg alloy, with an emphasis on the laser surface remelting (LSR) process. The experimental results demonstrate that the heat treatment degraded tensile strength while improving ductility by achieving grain growth and residual stress release. The yield strength obtained in the experiment was reduced from 200 to 100 MPa, whereas the elongation increased from 6 to 22%. The LSR process was found to contribute to an improvement in surface finish. The surface roughness indicator R_a was determined to be 0.93 μm in the LSR post-processed sample, compared to a fairly high value of 19.3 μm in the as-fabricated samples. The LSR process also enhanced the microhardness by refining the microstructure; the Si eutectic dendritic structure that formed was found to be finer than that of the as-fabricated samples. Compared to the as-fabricated samples, the LSR process contributed to a 19.5% increase in microhardness. The findings suggest that the microstructure and mechanical properties of SLM-fabricated AlSi10Mg parts could be tailored by suitable post-processing such as heat treatment and LSR. The significance of this research is its proposal of a novel technique to enhance surface hardness using LSR, which is a significant step towards the combination of SLM and LSR processes to manufacture customised aluminium components for the automotive and aerospace sectors.