Nanostructured NiO and Li-ion doped NiO have been synthesized via a facile microwave technique and simulated using the first principle method. The effects of microwaves on the morphology of the nanostructures have been studied by Field Emission Spectroscopy. X-ray diffraction studies confirm the nanosize of the particles and favoured orientations along the (111), (200) and (220) planes revealing the cubic structure. The optical band gap decreases from 3.3 eV (pure NiO) to 3.17 eV (NiO doped with 1% Li). Further, computational simulations have been performed to understand the optical behaviour of the synthesized nanoparticles. The optical properties of the doped materials exhibit violet, blue and green emissions, as evaluated using photoluminescence (PL) spectroscopy. In the presence of Li-ions, NiO nanoparticles exhibit enhanced electrical capacities and better cyclability. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) results show that with 1% Li as dopant, there is a marked improvement in the reversibility and the conductance value of NiO. The results are encouraging as the synthesized nanoparticles stand a better chance of being used as an active material for electrochromic, electro-optic and supercapacitor applications.

In this study, activated biochar was produced using pilot-scale technologies of fast pyrolysis and activation to create desirable morphology, surface chemistry, and adsorptive properties for application in supercapacitors. First, residues from white birch were converted into biochar by fast pyrolysis (~ 450 °C). Then, physical (using CO₂) or chemical (using KOH) activation was carried out in a homemade pilot-scale furnace at 900 °C. These synthesized materials presented distinct porosity structures: micro-/mesoporous (CO₂ material) and highly microporous (KOH material), reaching surface areas of up to 1700 m² g⁻¹. Electrochemical results showed that KOH-activated biochar had higher specific electrical capacitance in both acidic and neutral electrolytes with a maximum specific capacitance value of 350 and 118 F g⁻¹ at 1 A g⁻¹, respectively; while, for CO₂-activated biochar, the maximum obtained values were 204 and 14 F g⁻¹. The greater proportion of oxygenated and nitrogenated functional groups on the surface of the KOH activated biochar, along with its high surface area (with wider porosity), improved its performance as a supercapacitor electrode. Specifically, the low proportion of ultramicropores was determinant for its better electrochemical behavior, especially in the neutral electrolyte. Indeed, these results are similar to those found in the literature on the electrical capacitance of carbonaceous materials synthesized in a small-scale furnace. Thus, the chemical-activated biochar made from wood residues in pilot-scale furnaces is a promising material for use as electrodes for supercapacitors.

The increment of recycling of steel using electric arc furnace and the tendency to coat of steel products with zinc, in order to prevent corrosion, has increased the proportion of galvanized scrap used worldwide in the recent years. Approximately 10 to 20 Kg/t of cast steel is generated in casting arcs. These collected dusts electric arc furnace (EAF dust) contains iron, zinc, lead, and cadmium. Mainly in the form of oxides and their wastes are considered hazardous typically in countries such as Brazil, U.S., Japan and Germany. It is estimated that from the total of 7.5 million metric tons of EAF dust generated worldwide only 45% is recycled. With Waelz process, the EAF dust can be treated to recover zinc by means of reduction-volatilization-oxidation reactions occurring within the rotary kiln. In this work the thermodynamics of the Waelz process is studied to optimize the recovery of volatiles especially zinc. Kinetic parameters were evaluated trough series of ten experiments, comprise the major process factors such as type of reductants (charcoal and petroleum coke), time (20 – 120 minutes) and temperature (450 - 1150°C). The mechanical behavior of the pellets was evaluated by compressive cold strength and drop tests. Characterization was performed using scanning electron microscopy, microanalysis EDS, X-ray diffraction, X-ray fluorescence, granulometric analysis by laser diffraction, as well as measurements of moisture, bulk density and percentage of volatiles, fixed carbon and ash. The small pellets (10mm) with charcoal used as a reductant, presented a higher compression and higher recovery of volatiles than those with petroleum coke.