The outbreak of COVID-19 has spread rapidly across the globe, greatly affecting how humans as a whole interact, work and go about their daily life. One of the key pieces of personal protective equipment (PPE) that is being utilised to return to the norm is the face mask or respirator. In this review we aim to examine face masks and respirators, looking at the current materials in use and possible future innovations that will enhance their protection against SARS-CoV-2. Previous studies concluded that cotton, natural silk and chiffon could provide above 50% efficiency. In addition, it was found that cotton quilt with a highly tangled fibrous nature provides efficient filtration in the small particle size range. Novel designs by employing various filter materials such as nanofibres, silver nanoparticles, and nano-webs on the filter surfaces to induce antimicrobial properties are also discussed in detail. Modification of N95/N99 masks to provide additional filtration of air and to deactivate the pathogens using various technologies such as low- temperature plasma is reviewed. Legislative guidelines for selecting and wearing facial protection are also discussed. The feasibility of reusing these masks will be examined as well as a discussion on the modelling of mask use and the impact wearing them can have. The use of Artificial Intelligence (AI) models and its applications to minimise or prevent the spread of the virus using face masks and respirators is also addressed. It is concluded that a significant amount of research is required for the development of highly efficient, reusable, anti-viral and thermally regulated face masks and respirators.

Electrospun nanofibrous mats consisting of chitosan (CS) and polyvinylpyrrolidone (PVP) were constructed. Tuning of solution and process parameters was performed and resulted in an electrospun system containing a 6:4 ratio of PVP:CS. This is a significant increase in the proportion of spun CS on the previously reported highest ratio PVP:CS blend. SEM analysis showed that the nanofibrous mats with 4 wt% CS/6 wt% PVP (sample E) comprised homogenous, uniform fibres with an average diameter of 0.569 μm. XPS analysis showed that the surface of the samples consisted of PVP. Raman and FTIR analysis revealed intermolecular interactions (via H-bonding) between PVP and CS. In FTIR spectra, the contribution of chitosan to CS/PVP complexes was shown by the downshift of the C=O band and by the linear increase in intensity of C-O stretching in CS. XPS analysis showed a smaller shift at the binding energy 531 eV, which relates to the amide of the acetylated functional groups. The obtained results demonstrate a sensitivity of Raman and FTIR tests to the presence of chitosan in PVP:CS blend. The chemotherapy drug 5-Fu was incorporated into the constructs and cell viability studies were performed. WST-8 viability assay showed that exposure of A549 human alveolar basal epithelial cells to 10 mg/mL 5-Fu loaded fibres was most effective at killing cells over 24 h. On the other hand, the constructs with loading of 1 mg/mL of drug were not efficient at killing A549 human alveolar basal epithelial cells. This study showed that CS/PVP/5-Fu constructs have potential in chemotherapeutic drug delivery systems.