The effect of TiO₂ nanostructures such as nanoparticles, nanowires, nanotubes on photoanode properties, and dye-sensitized solar cells photovoltaic parameters were studied. The series of dye-sensitized solar cells based on two dyes, that is, commercially N719 and synthesized 3,7′-bis(2-cyano-1-acrylic acid)-10-ethyl-phenothiazine were tested. Additionally, the devices containing a mixture of this sensitizer and chenodeoxycholic acid as co-adsorbent were fabricated. The amount of adsorbed dye molecules to TiO₂ was evaluated. The prepared photoanodes with different TiO₂ nanostructures were investigated using UV-Vis spectroscopy, optical, atomic force, and scanning electron microscopes. Photovoltaic response of constructed devices was examined based on current-voltage characteristics and electrochemical impedance spectroscopy measurements. It was found that the highest UV-Vis absorption exhibited the photoanode with nanotubes addition. This indicates the highest number of sensitizer molecules anchored to the titanium dioxide photoanode, which was subsequently confirmed by dye-loading tests. The highest power conversion efficiency was (6.97%) for solar cell containing nanotubes and a mixture of the dyes with a co-adsorbent.

The article presents the thermal and physical properties of PMMA composite films with the addition of Nb₂O₅ nanoparticles. The addition of nanoparticles to PMMA mainly influenced the optical transmission and glass transition temperature of composite films compared to pure PMMA. It is clearly visible in the results of the conducted ellipsometric and differential scanning calorimetry tests. X-ray studies showed that the heat treatment of the samples resulted in the ordering of the polymer structure (flattening of the polymer chains). Examining the surface of the samples with scanning electron microscopy, it can be seen that Nb₂O₅ nanoparticles formed unusual, branched formations resembling "snowflakes".

We report the phase behavior of amorphous/semicrystalline conjugated polymer blends composed of low bandgap poly[2,6-(4,4-bis(2-ethylhexyl)-4H-cyclopenta [2,1-b;3,4-b′]dithiophene) -alt-4,7(2,1,3-benzothiadiazole)] (PCPDTBT) and poly{(N,N′-bis(2-octyldodecyl)naphthalene -1,4,5,8-bis(dicarboximide)-2,6-diyl)-alt-5,5′-(2,2′-bithiophene)} (P(NDI2OD-T2)). As usual in polymer blends, these two polymers are immiscible because ΔS_m ≈ 0 and ΔH_m > 0, leading to ΔG_m > 0, in which ΔS_m, ΔH_m, and ΔG_m are the entropy, enthalpy, and Gibbs free energy of mixing, respectively. Specifically, the Flory–Huggins interaction parameter (χ) for the PCPDTBT /P(NDI2OD-T2) blend was estimated to be 1.26 at 298.15 K, indicating that the blend was immiscible. When thermally analyzed, the melting and crystallization point depression was observed with increasing PCPDTBT amounts in the blends. In the same vein, the X-ray diffraction (XRD) patterns showed that the π-π interactions in P(NDI2OD-T2) lamellae were diminished if PCPDTBT was incorporated into the blends. Finally, the correlation of the solid-liquid phase transition and structural information for the blend system may provide insight for understanding other amorphous/semicrystalline conjugated polymers used as active layers in all-polymer solar cells, although the specific morphology of a film is largely affected by nonequilibrium kinetics.

In recent years, perovskite solar cells (PSCs) have gained major attention as potentially useful photovoltaic technology due to their ever-increasing power-conversion efficiency (PCE). The efficiency of PSCs depends strongly on the type of materials selected as the electron transport layer (ETL). TiO₂ is the most widely used electron transport material for the n-i-p structure of PSCs. Nevertheless, ZnO is a promising candidate owing to its high transparency, suitable energy band structure, and high electron mobility. In this investigation, hybrid mesoporous TiO₂/ZnO ETL was fabricated for a perovskite solar cell composed of FTO-coated glass/compact TiO₂/mesoporous ETL/FAPbI₃/2D perovskite/Spiro-OMeTAD/Au. The influence of ZnO nanostructures with different percentage weight contents on the photovoltaic performance was investigated. It was found that the addition of ZnO had no significant effect on the surface topography, structure, and optical properties of the hybrid mesoporous electron-transport layer but strongly affected the electrical properties of PSCs. The best efficiency rate of 18.24% has been obtained for PSCs with 2 wt.% ZnO.

This work focuses on the study of thermal and physical properties of thin polymer films based on mixtures of semiconductor polymers. The materials selected for research were poly [2,5-bis(2-octyldodecyl)-pyrrolo [3,4-c]pyrrole-1,4(2H,5H)-dione-3,6-diyl)-alt-(2,2′;5′,2″;5″,2′′′-quater-thiophen-5,5′′′-diyl)]—PDPP4T, a p-type semiconducting polymer, and poly(2,5-bis(2-octyldodecyl)-3,6-di(pyridin-2-yl)-pyrrolo [3,4-c]pyrrole-1,4(2H,5H)-dione-alt-2,2′-bithiophene)—PDBPyBT, a high-mobility n-type polymer. The article describes the influence of the mutual participation of materials on the structure, physical properties and thermal transitions of PDPP4T:PDBPyBT blends. Here, for the first time, we demonstrate the phase diagram for PDPP4T:PDBPyBT blend films, constructed on the basis of variable-temperature spectroscopic ellipsometry and differential scanning calorimetry. Both techniques are complementary to each other, and the obtained results overlap to a large extent. Our research shows that these polymers can be mixed in various proportions to form single-phase mixtures with several thermal transitions, three of which with the lowest characteristic temperatures can be identified as glass transitions. In addition, the RMS roughness value of the PDPP4T:PDBPyBT blended films was lower than that of the pure materials.

The results of studies on the influence of zinc oxide nanoparticles (ZnO-NPs) on the structural, thermal and optical properties of thin films of mixtures of phenyl-C71-butyric acid methyl ester (PCBM) with poly[3-hexylthiophene] (P3HT) of various molecular weights are described in this article. The structural properties of the layers of: polymers, mixtures of polymers with fullerenes and their composites with ZnO-NPs were investigated using X-ray diffraction. Whereas their glass transition temperature and optical parameters have been determined by temperature-dependent spectroscopic ellipsometry. The presence of ZnO-NPs was also visible in the images of the surface of the composite layers obtained using scanning electron microscopy. These blends and composite films have also been used as the active layer in bulk heterojunction photovoltaic structures. The molecular weight of P3HT (Mw = 65.2; 54.2 and 34.1 kDa) and the addition of nanoparticles affected the power conversion efficiency (PCE) of the obtained solar cells. The determined PCE was the highest for the device prepared from the blend of P3HT:PCBM with the polymer of the lowest molecular weight. However, solar cells with ZnO-NPs present in their active layer had lower efficiency, although the open-circuit voltage and fill factor of almost all devices had the same values whether they contained ZnO-NPs or not. It is worth noting that thermal studies carried out using temperature-dependent ellipsometry showed a significant effect of the presence of ZnO-NPs on the value of the glass transition temperature, which was higher for composite films than for films made of a polymer-fullerene blend alone.