In this study, we investigate the interactions between the cellulose surface and Ag nanoparticles (AgNPs) for the purpose of manufacturing hybrid nanomaterials using bacterial cellulose nanocrystals (BCNs) as a model substrate. We focus on the role of the BCN surface chemistry on the AgNP nucleation obtained by chemical reduction of Ag+ ions. Homogeneous hybrid suspensions of BCN/AgNP are produced, regardless of whether the BCNs are quasi-neutral, negatively (TBCNs) or positively charged (ABCNs). The characterization of BCN/AgNP hybrids identifies the -OH surface groups as nucleation points for AgNPs, of about 20 nm revealing that surface charges only improve the accessibility to OH groups. X-ray Absorption technics (XANES and EXAFS) revealed a high metallic Ag0 content ranging from 88% to 97%. Moreover, the grafting of hydrophobic molecules on a BCN surface (HBCNs) does not prevent AgNP nucleation, illustrating the versatility of our method and the possibility to obtain bifunctional NPs. A H2O2 redox post-treatment on the hybrid induces an increase in AgNPs size, up to 90 nm as well as a shape variation (i.e., triangular). In contrast, H2O2 induces no size/shape variation for aggregated hybrids, emphasizing that the accessibility to -OH groups ensures the nucleation of bigger Ag nano-objects.

There is a demand for nanoparticles that are environmentally acceptable, but simultaneously efficient and low cost. We prepared silver nanoparticles (AgNPs) grafted on a native bio-based substrate (cellulose nanocrystals, CNCs) with high biocidal activity and no toxicological impact. AgNPs of 10 nm are nucleated on CNCs in aqueous suspension with content from 0.4 to 24.7 wt%. XANES experiments show that varying the NaBH4/AgNO3 molar ratio affects the AgNP oxidation state, while maintaining an fcc structure. AgNPs transition from 10 nm spherical NPs to 300 nm triangular-shaped AgNPrisms induced by H₂O₂ post-treatment. The 48 h biocidal activity of the hybrid tested on B. Subtilis is intensified with the increase of AgNP content irrespective of the Ag⁺/Ag₀ ratio in AgNPs, while the AgNSphere−AgNPrism transition induces a significant reduction of biocidal activity. A very low minimum inhibitory concentration of 0.016 mg AgNP/mL is determined. A new long-term biocidal activity test (up to 168 h) proved efficiency favorable to the smaller AgNPs. Finally, it is shown that AgNPs have no impact on the phagocytic capacity of mammalian cells.

Hybrid nanoparticles involving 10-nm silver nanoparticles (AgNPs) nucleated on unmodified rod-like cellulose nanocrystals (CNCs) were prepared by chemical reduction. H₂O₂ used as a post-treatment induced a size-shape transition following a redox mechanism, passing from 10-nm spherical AgNPs to 300-nm triangular or prismatic NPs (AgNPrisms), where CNCs are the only stabilizers for AgNPs and AgNPrisms. We investigated the role of the H₂O₂/AgNP mass ratio (α) on AgNPs. At α values above 0.20, the large amount of H₂O₂ led to extensive oxidation that produced numerous nucleation points for AgNPrisms on CNCs. On the contrary, for α below 0.20, primary AgNPs are only partially oxidized, releasing a reduced amount of Ag⁺ ions and thus preventing the formation of AgNPrisms and reforming spherical AgNPs. While XRD and EXAFS reveal that the AgNP fcc crystal structure is unaffected by the H₂O₂ treatment, the XANES spectra proved that the AgNP–AgNPrism transition is always associated with an increase in the metallic Ag fraction (Ag₀). In contrast, the formation of new 15-nm spherical AgNPs keeps the initial Ag₀/Ag⁺ ratio unmodified. For the first time, we introduce a complete guide map for the fully-controlled preparation of aqueous dispersed AgNPs using CNC as a template.