Al_xGa_1−xN/GaN heterostructures with two kinds of Al composition were grown by metal organic chemical vapor deposition (MOCVD) on sapphire substrates. The Al compositions in the AlGaN barrier layer were confirmed to be 13% and 28% using high resolution X-ray diffraction (HRXRD). Al_xGa_1−xN/GaN high-electron mobility transistors (HEMTs) with different Al compositions were fabricated, characterized, and compared using the Hall effect, direct current (DC), and low-frequency noise (LFN). The device with high Al composition (28%) showed improved sheet resistance (R_sh) due to enhanced carrier confinement and reduced gate leakage currents caused by increased Schottky barrier height (SBH). On the other hand, the reduced noise level and the low trap density (N_t) for the device of 13% of Al composition were obtained, which is attributed to the mitigated carrier density and decreased dislocation density in the Al_xGa_1−xN barrier layer according to the declined Al composition. In spite of the Al composition, the fabricated devices exhibited 1/ƒ noise behavior with the carrier number fluctuation (CNF) model, which is proved by the curves of both (S_Id/I_d²) versus (g_m/I_d)² and (S_Id/I_d²) versus (V_gs–V_th). Although low Al composition is favorable to the reduced noise, it causes some problems like low R_sh and high gate leakage current. Therefore, the optimized Al composition in AlGaN/GaN HEMT is required to improve both noise and DC properties.

We investigated the effects of GaN buffer resistance of AlGaN/GaN high-electron-mobility transistors (HEMTs) on direct current (DC), low-frequency noise (LFN), and pulsed I-V characterization performances. The devices with the highest GaN buffer resistance were grown on sapphire substrate using two-step growth temperature method without additional compensation doping. The proposed device exhibited the degraded off-state leakage current due to the improved GaN buffer quality compared to the reference devices with relative low buffer resistance, which is confirmed by high resolution X-ray diffraction (HRXRD). However, the proposed device with deep-level defects in GaN buffer layer showed the reduced hysteresis (∆V_th), increased breakdown voltage (BV), and enhanced pulse I-V characteristics. Regardless of GaN buffer resistance, all devices clearly showed 1/f behavior with carrier number fluctuations (CNF) at on-state but followed 1/f² characteristic at off-state. From the 1/f² noise characteristics, the extracted trap time constant (τ_i) of the proposed device can be obtained to be 10 ms, which is shorter than those of the reference devices because of the full compensation of deep-level defects in the GaN buffer layer.

We investigated the effects of in situ silicon carbon nitride (SiCN) cap layer of AlGaN/GaN high-electron mobility transistors (HEMTs) on DC, capacitance-voltage (C-V) and low-frequency noise (LFN). The proposed device with SiCN cap layer exhibited enhanced drain current, reduced gate leakage current, low interface trap density (D_it), and high on/off ratio thanks to the passivation effect, compared to the device without SiCN cap layer. Both devices clearly showed 1/f noise behavior with carrier number fluctuations (CNF), regardless of the existence of SiCN cap layer. The proposed device presented the relative low trap density (N_it) and reduced access noise due to the effective surface passivation in source-drain access region compared to the device without SiCN cap layer. From the improved DC, C-V and noise results of the proposed device, the in situ SiCN cap layer plays an important role in the passivation layer and gate oxide layer in AlGaN/GaN HEMT.

For the creation of next-generation nanoscale devices, it is crucial to comprehend the carrier transport mechanisms in nanowires. Here, we examine how temperature affects the properties of GaN nanowire wrap-gate transistors (WGTs), which are made via a top-down technique. The predicted conductance in this transistor remains essentially unaltered up to a temperature of 240 K and then increases after that as the temperature rises. This is true for increasing temperature at gate voltages less than threshold voltage (V_gs < V_th). Sharp fluctuations happen when the temperature rises with a gate voltage of V_th < V_gs < V_FB. The conductance steadily decreases with increasing temperature after increasing the gate bias to V_gs > V_FB. These phenomena are possibly attributed to phonon and impurity scattering processes occurring on the surface or core of GaN nanowires.

It is essential to understand the barrier height, ideality factor, and role of inhomogeneities at the metal/semiconductor interfaces in nanowires for the development of next generation nanoscale devices. Here, we investigate the drain current (I_ds)–gate voltage (V_gs) characteristics of GaN nanowire wrap-gate transistors (WGTs) for various gate potentials in the wide temperature range of 130–310 K. An anomalous reduction in the experimental barrier height and rise in the ideality factor with reducing the temperature have been perceived. It is noteworthy that the variations in barrier height and ideality factor are attributed to the spatial barrier inhomogeneities at the AlGaN/GaN interface in the GaN nanowire WGTs by assuming a double Gaussian distribution of barrier heights at 310–190 K (distribution 1) and 190–130 K (distribution 2). The standard deviation for distribution 2 is lower than that of distribution 1, which suggests that distribution 2 reflects more homogeneity at the AlGaN/GaN interface in the transistor’s source/drain regions than distribution 1.

A tetramethyl ammonium hydroxide (TMAH)-treated normally-off Gallum nitride (GaN) metal-insulator-semiconductor field-effect transistor (MISFET) was fabricated and characterized using low-frequency noise (LFN) measurements in order to find the conduction mechanism and analyze the trapping behavior into the gate insulator as well as the GaN buffer layer. At the on-state, the noise spectra in the fabricated GaN device were 1/f^γ properties with γ ≈ 1, which is explained by correlated mobility fluctuations (CMF). On the other hand, the device exhibited Lorentzian or generation-recombination (g-r) noises at the off-state due to deep-level trapping/de-trapping into the GaN buffer layer. The trap time constants (τ_i) calculated from the g-r noises became longer when the drain voltage increased up to 5 V, which was attributed to deep-level traps rather than shallow traps. The severe drain lag was also investigated from pulsed I-V measurement, which is supported by the noise behavior observed at the off-state.