A novel red emitting, Ce ³⁺ -activated Sr ₃ Sc ₄ O ₉ phosphor were discovered, and its luminescent properties were investigated.

Obtaining highly efficient photoluminescence with Mn⁴⁺-activated phosphors, which have been extensively studied in diverse lighting devices, requires the precise control of the manganese valence states. However, this control is difficult to achieve because manganese ions can have various valence states ranging from divalent to heptavalent. Additionally, the concentrations of Mn ions in each valence state, especially the effective Mn⁴⁺ concentration, have never been quantitatively determined in a phosphor crystal lattice. The relationship between the effective Mn⁴⁺ concentration and the luminescence properties of Mn⁴⁺-activated phosphors is of current interest for improving the phosphor properties. In the present study, the effective Mn⁴⁺ concentration in Li₂TiO₃:Mn⁴⁺ (LTO:Mn) phosphors prepared by the sol–gel method with heating at various temperatures was quantitatively analyzed by X-ray absorption near-edge spectroscopy. Moreover, the effect of the existence of Mn²⁺, Mn³⁺, and Mn⁴⁺ ions on the photoluminescence efficiency was investigated. The effective Mn⁴⁺ concentration was found to be over 60% in all phosphor samples. The quantum efficiencies (QEs) of all LTO:Mn phosphors strongly depend on the effective Mn⁴⁺ concentration. In particular, the LTO:Mn phosphor prepared by heating at 800 °C (LTO:[email protected]) contained the highest effective Mn⁴⁺ concentration of 98.1% and exhibited the highest internal QE of 31.6%. The results of this work provide new and important insights for the development of Mn⁴⁺-activated phosphors with high efficiency.

A novel red-emitting olivine-type NaMgPO₄:Eu²⁺ phosphor was synthesized for the first time by the melt synthesis technique using arc-imaging furnace. The NaMgPO₄:Eu²⁺ phosphor can be efficiently excited by blue light irradiation and presents red emission band centered at 628 nm due to the 4f⁶5d¹ → 4f⁷ transition of Eu²⁺. The highest emission peak intensity was obtained for NaMgPO₄:2.5mol%Eu²⁺, and the internal quantum efficiency of this phosphor at the excitation wavelength of 450 nm was 81%. Furthermore, these phosphors show an excellent thermal stability on the temperature quenching effect.