Natural fiber polymer matrix composites occupy the major percentage in applications due to its ecofriendly and low-cost nature. This study investigates the mechanical properties of a polyester matrix nanocomposite reinforced by the NaOH-treated jute fabric mat (NJM) and untreated jute fabric mat (UJM). In addition, the effects of egg shell powder (ESP) and nanoclay (NC) to the above has also been studied. The matrices were prepared with different combinations of presence and absence of the ESP, NC, and both as well as different weight percentage using compression molding process. The mechanical and morphological properties of the composites were determined. The tensile strength, flexural strength, and impact strength of NJM with NC 1.5%wt and ESP 1.5%wt were found to be 29.28 MPa, 39.51 MPa and impact strength 3.03 J, respectively. This composition is superior to the other compositions. Morphological analysis of tensile fractured surface showed interfacial adhesion between UJM and NJM composites. NJM composites contained smaller amount of pullouts and the splits compared with the UJM composites, which hold up the better performance.

Composite materials, made by replacing traditional materials, are used because of their capability to produce tailor-made, desirable properties such as high tensile strength, low thermal expansion, and high strength to weight ratio. The need for the development of new materials is essential and growing day by day. The natural sisal/general polymer (GP) reinforced with nanoclay composites has become more attractive due to its high specific strength, light weight, and biodegradability. In this study, sisal–nanoclay composite is developed and its mechanical properties such as tensile strength, flexural strength, and impact strength are evaluated. The interfacial properties, internal cracks, and internal structure of the fractured surface are evaluated using scanning electron microscope. The thermal disintegration of composites are evaluated by thermogravimetric analysis. The results indicate that the incorporation of nanoclay in sisal fiber/GP can improve its properties and can be used as a substitute material for glass fiber-reinforced polymer composites.