Controlling bacterial biofilm formation on silicone-based bloodstream catheters is of great concern to prevent related-infections. In this study, rhamnolipids (RLs), glycolipid biosurfactants, specifically a RLs mixture and the purified di-RL (RhaRhaC10:0C10:0) were covalently bonded to silicone with the intention of reaching long-lasting antibiofilm surfaces. RLs mixture and di-RL were identified by an UHPLC-MS method that also allowed the confirmation of compound isolation by automated flash chromatography. Silicone surfaces underwent air-plasma treatment, inducing reactive oxygen radicals able to promote the RLs grafting that was confirmed by contact angle, FTIR-ATR and AFM measurements. The antibiofilm activity towards different Gram positive strains was evaluated by colony forming units (CFU) count and confocal laser microscopy. In addition, protein adsorption and biocompatibility were also investigated. RLs were successfully grafted onto silicone and RLs mixture and RhaRhaC10C10:0 functionalized specimens reduced the biofilm formation over 2.3 log units against methicillin sensitive Staphylococcus aureus. Additionally, a decrease of 1 log unit was observed against methicillin resistant S. aureus and S. epidermidis. Functionalized samples showed cytocompatibility towards human dermal fibroblasts, hemocompatibility and no vascular irritation potential. The results mentioned above revealed a synergy between the antimicrobial and the anti-adhesive properties of RLs, making these compounds good candidates for the improvement of the medical devices antibiofilm properties.

In clinic there is a demand to solve the drawback of medical devices multispecies related infections. Consequently, different biomaterial surfaces, such as vascular catheters, urgently need improvement regarding their antifouling/antimicrobial properties. In this work, we covalently functionalized medical grade polydimethylsiloxane (PDMS) with antimicrobial rhamnolipids to investigate the biomaterial surface activity towards mono and dual species biofilms. Preparation of surfaces with "piranha" oxidation, followed by APTES bonding and carbodiimide reaction with rhamnolipids effectively bonded these compounds to PDMS surface as confirmed by FTIR-ATR and XPS analysis. Generated surfaces were active towards S. aureus biofilm formation showing a 4.2 log reduction while with S. epidermidis and C. albicans biofilms a reduction of 1.2 and 1.0 log reduction, respectively, was observed. Regarding dual-species testing the higher biofilm log reduction observed was 1.9. Additionally, biocompatibility was assessed by cytocompatibility towards human fibroblastic cells, low platelet activation and absence of vascular irritation. Our work not only sheds light on using covalently bonded rhamnolipids towards dual species biofilms but also highlights the biocompatibility of the obtained PDMS surfaces.