The effect of polyvinylpyrrolidone (PVP) as glycyrrhetic acid (GA) solid dispersions carrier at different molecular weights on the dissolution behavior and physicochemical properties was investigated. PVP-GA-SDs prepared with all four molecular weight PVPs displayed good enhancement of dissolution rate and equilibrium solubility compared with pure drug and corresponding physical mixtures. The results showed that the enhancement effect of molecular weight on dissolution rate and equilibrium solubility follows . In addition, the dissolution rate and solubility of the SDs with a carrier-drug ratio of 8 : 1 were better than the samples of 4 : 1. The DSC and XRD patterns showed that the crystallization of GA in SDs prepared by PVP K30 and PVP K60 was significantly inhibited, and both were transformed to amorphous. Based on FTIR and Raman detection, a hydrogen-bond between PVP and drug molecules is formed. SEM results showed that there were no significant differences in the appearance of SDs prepared with four PVPs, and no crystalline morphology of GA was seen. In conclusion, the findings of this study demonstrated that the dissolution performance of the PVP-GA-SDs prepared by the solvent method is related to the molecular weight of PVP, and the change in the molecular weight of PVP does not cause a monotonic change in dissolution of GA. The samples with PVP K30 as the carrier have the best dissolution performance.

Applicability of multi‑walled carbon nanotubes (MWCNTs) in loading dipyridamole (DDM), a poorly soluble drug, was evaluated. Additionally, the effect of drug‑loading efficiency on the release behavior of the MWCNT‑DDM system was also investigated. DDM as a model drug was incorporated into MWCNTs with different drug‑loading rates (10, 25 and 50%) using the solvent deposition method. The MWCNT‑DDM system was successfully established and characterized using common solid‑state characterization methods. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption analysis and Fourier transform‑infrared (FT‑IR) spectroscopy were carried out to observe the progress of drug loading. X‑ray diffraction (XRD) and differential scanning calorimetry (DSC) were used to systematically assess the crystalline state of the DDM after being loaded into the MWCNTs. Improvements in dissolution rate were evaluated by the dissolution test. The results revealed that with the increase of drug loading, the form of DDM in the MWCNTs changed from amorphous to crystalline state. Also, the release rate of DDM decreased upon increasing the drug‑loading rate of carriers. In conclusion, MWCNTs are proven to be promising carriers for loading DDM.

Past studies have shown that the hot spring effect can promote wound healing. Mild thermal stimulation and metal ions can promote angiogenesis. In this study, the hot spring effect was simulated by thermosensitive PNIPAAm hydrogel loaded with copper sulfide nanoparticles. Heat stimulation could be generated through near-infrared irradiation, and copper ions solution could be pulsed. On the other hand, the CS/PVA nanofiber membrane was attached to the bottom of the hydrogel to simulate the extracellular matrix structure, thus improving the wound healing ability. The CS/PVA nanofiber membrane was prepared by electrospinning, and the appropriate prescription and process parameters were determined. The nanofiber membrane has uniform pore size, good water absorption and permeability. The poor mechanical properties of PNIPAAm hydrogel were improved by adding inorganic clay. The temperature of the hydrogel loaded with CuS nanoparticles reached 40 °C under near-infrared light irradiation for 20 min, and the release rate of Cu²⁺ reached 26.89%. The wound-healing rate of the rats in the combined application group reached 79.17% at 13 days, demonstrating superior results over the other control groups. Histological analyses show improved inflammatory response at the healed wound area. These results indicate that this combined application approach represents a promising wound treatment strategy.