Fe-30Mn-0.05C steel specimens with cold-rolled, partially recrystallized, fine-grained, and coarse-grained microstructures were fabricated by means of 80% cold rolling followed by annealing at 550–1000 °C. The initial and deformed microstructures were characterized, and the Charpy impact properties were tested at room temperature (RT) and liquid nitrogen temperature (LNT). It was found that the Charpy absorbed energy increased with the annealing temperature, while the specimens showed different trends: parabolic increase at RT and exponential increase at LNT, respectively. Compared with the fully recrystallized specimens, those with a partially recrystallized microstructure exhibited lower impact energy, especially at LNT. This was because cracks tended to nucleate and propagate along the recovery microstructure where stress concentration existed. The grain size played an important role in the twinning behavior and impact properties. High Charpy impact energy (~320 J) was obtained in the coarse-grained specimen having the grain size of 42.1 μm at both RT and LNT, which was attributed to the activation of high-density deformation twinning. However, deformation twinning was inhibited in the specimen with the average grain size of 3.1 μm, resulting in limited work hardening and lower impact energy.

The present study employed numerical simulation technology to investigate the distribution of workpieces within a low-temperature trolley heat furnace and analyze the influence of circulating fan parameters on heat treatment quality. This analysis was integrated with machine learning technology to guide heat treatment production. The research findings indicate that when the number of workpieces remains constant, their position has a significant impact on airflow velocity distribution, heating rate, and temperature uniformity within the furnace. Additionally, wind pressure from the circulating fan affects both fluid field and temperature field; the increasing wind pressure leads to higher flow rates in the furnace as well as increases heating rates for workpieces. Heating efficiency exhibits a nonlinear relationship with wind pressure increment. By adjusting air pressure distribution from the circulating fan, workpiece temperature uniformity can be improved by 64%. Furthermore, machine learning technique demonstrates excellent performance in predicting workpiece temperatures with a maximum relative error of 2.4%, while maintaining consistent trends in temperature uniformity.

High temperature confocal laser scanning microscopy (CLSM) was used to investigate the microstructure evolution of high-strength boron steel 22MnB5 during hot stamping. The experimental results show that it is complete austenitized at temperatures about 810 °C during the heating process. Most of the initial austenite grain size is small and locally coarse. At 920 °C to 1000 °C, the phenomenon of B remelted and solidified was observed which played a very good pinning role at the austenite grain boundary, preventing coarsening of austenite grains. The segregation of B and the addition of Mn result in a significant reduction in both the minimum boron reverse melt content and the final solidification temperature. In the continuous cooling stage, martensitic transformation occurs at the cooling rate of 60 °C/s, and the martensite start point is 400 °C and martensite finish point is 280 °C. A large number of bursts are concentrated from 380 °C to 330 °C. There are two main forms of martensitic transformation: first, martensite begins to appear at the coarse austenite grain boundary, and grows transgranularly. Second, the new martensite laths starts from the previously formed laths and grows at a certain angle into the austenite grains. The main factor in the increase of martensite in continuous cooling is the formation of variable temperature martensite rather than the growth of martensite laths. At the cooling rate of 20 °C/s, the bainite and ferrite transformation appeared and the conversion temperature of bainite was about 600 °C. The cooling speed has a great influence on the performance of the 22MnB5 hot stamping component. The room temperature microhardness at cooling rates of 5 °C/s, 20 °C/s, and 60 °C/s was 194 HV, 243 HV, and 430 HV, respectively. Therefore, ensuring sufficient cooling rate is a key condition for obtaining ultra-high strength hot stamping components.

Traditional hot-stamping products have super-high strength, but their plasticity is usually low and their integrated mechanical properties are not excellent. Functionally graded property structures, a relatively novel configuration with a higher material utilization rate, have increasingly captured the attention of researchers. Hot stamping parts with tailored properties display the characteristics of local high strength and high plasticity, which can make up for the limitations of conventional hot stamping and optimize the crash safety performance of vehicles. This new idea provides a means of personalized control in the hot-stamping process. In this paper, a new strategy of local induction heating and press hardening was used for the hot stamping of boron steel parts with tailored properties, of which the microstructure from the hard zone to the soft zone shows a gradient distribution consisting of a martensite phase, multiphase and initial phase, with the hardness ranging from 550 HV to 180 HV. The re-deformation characteristics of hot stamping parts with tailored properties have been studied through the uniaxial tensile test, in cooperation with digital image correlation (DIC) and electron backscattered diffraction (EBSD) techniques. The experiments show that there are easily observable strain distribution characteristics in the re-deformation of hot stamping parts with tailored properties. In the process of tensile deformation, the initial phase zone takes the role of deformation and energy absorption, with the maximum strain before necking reaching 0.32. The local misorientation of this zone was high, and a large number of low angle grain boundaries were formed, while the proportion of small angle grain boundaries increased from 13.5% to 63.3%, and the average grain size decreased from 8.15 μm to 3.43 μm. Meanwhile, the martensite zone takes on the role of anti-collision protection, with a maximum strain of only 0.006, and its local misorientation is mostly unchanged. The re-deformation experimental results show that the hot stamping of boron steel parts with tailored properties meets the functional requirements of a hard zone for anti-collision and a soft zone for energy absorption, suitable for automobile safety parts.

An Fe-0.15C-1.2Si-5Mn-0.09Nb-0.08V-0.07Mo (wt.%) medium manganese steel that was subjected to a novel austenite reverted transformation (ART) annealing process. This paper is based on the conventional ART annealing process, and a deformation and ART annealing process is proposed. The influence of the deformation degree on the microstructure and grain size of the medium manganese steel was determined by scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD) and X-ray diffraction (XRD). The results show that the deformation had a great effect on the microstructure evolution and grain size. The microstructure of the medium manganese steel after the deformation and ART annealing process was consistent with the theory of austenite reverse transformation, i.e., the martensite reverse transformation into austenite occurred during the deformation and ART annealing process. The final microstructure was a mixture of martensite and austenite. As the deformation degree increases, the martensite gradually refines, and carbides precipitate in the lath martensite. The retained austenite is gradually transformed from very large to small and is distributed between the martensite laths. The results show that when deformation occurs in the austenite region, a small deformation can obtain more retained austenite.