Atmospheric concentrations of carbon dioxide (CO2), a major cause of global warming, have been rising due to industrial development. Carbon capture and storage (CCS), which is regarded as the most effective way to reduce such atmospheric CO2 concentrations, has several environmental and technical disadvantages. Carbon capture and utilization (CCU), which has been introduced to cover such disadvantages, makes it possible to capture CO2, recycling byproducts as resources. However, CCU also requires large amounts of energy in order to induce reactions. Among existing CCU technologies, the process for converting CO2 into CaCO3 requires high temperature and high pressure as reaction conditions. This study proposes a method to fixate CaCO3 stably by using relatively less energy than existing methods. After forming NaOH absorbent solution through electrolysis of NaCl in seawater, CaCO3 was precipitated at room temperature and pressure. Following the experiment, the resulting product CaCO3 was analyzed with Fourier transform infrared spectroscopy (FT-IR); field emission scanning electron microscopy (FE-SEM) image and X-ray diffraction (XRD) patterns were also analyzed. The results showed that the CaCO3 crystal product was high-purity calcite. The study shows a successful method for fixating CO2 by reducing carbon dioxide released into the atmosphere while forming high-purity CaCO3.

Anion exchange membranes were synthesized from different compositions of glycidyl methacrylate (GMA) and vinylbenzyl chloride (VBC), with constant content of divinyl benzene (DVB) by radical polymerization using benzoyl peroxide (BPO) on non-woven polyethylene terephthalate (PET) substrate. Polymerized membranes were then quaternized by soaking in trimethylamine (TMA), triethylamine (TEA), tripropylamine (TPA), and 1,4-diazabicyclo [2.2.2] octane (DABCO). Characteristics of membranes were confirmed by Fourier transform infrared spectroscopy, water uptake, ion exchange capacity, ion conductivity, thermal, and alkaline stability. The results revealed that membranes quaternized by TPA and DABCO showed high affinity when GMA content was 15 wt% and 75 wt%, respectively. IEC and ion conductivity of membranes quaternized by TPA were 1.34 meq·g⁻¹ and 0.022 S·cm⁻¹ (at 60 °C), respectively. IEC and ion conductivity of membranes were quaternized by DABCO were 1.34 meq·g⁻¹ and 0.021 S·cm⁻¹ (at 60 °C), respectively. The results indicate that the membrane containing GMA 15 wt% quaternized by TPA showed the highest thermal stability among membranes and exhibited high ion conductivity compared to existing researches using GMA, VBC, and DVB monomers.