The need to increase the durability of clay-based materials, due to their inherent low strength and vulnerability in contact with water, led researchers to examine different options. In this paper, clay mortars were produced using four different activating solutions. Alkali hydroxides, alkali carbonates, and alkali silicates activating solutions were used. Interest is given to long term properties while their behavior to wetting–drying and freeze–thaw cycles is recorded. In total, the results of the experiments indicated the positive effect of the potassium metasilicate on mechanical characteristics presenting, however, low performance at wetting–drying. The combination of sodium metasilicate with sodium hydroxide solution has also presented a positive effect on both mechanical and physical properties. In contrast, sodium carbonate acted better in enhancing physical properties and granting water-resistant abilities. Moreover, the performance of the specimens mixed with water–glass addition presented excellent volume stability and low mass loss in durability tests.

The present study proposes nano-calcium oxide (NC) and nano-silica (NS) particles as healing agents in cement pastes, taking into account the curing conditions. Two series of specimens were treated in water and under wetting-drying cycles. The addition of NC (1.5%wt of binder) triggered early healing since cracks were healed within 14 days in underwater immersion and before 28 days at wetting-drying cycles. Attenuated Total Reflectance (ATR) spectroscopy and SEM analysis revealed that the healing products were mainly aragonite and calcite in water conditions and more amorphous carbonates under wetting-drying cycles. The combination of NS and NC (3.0%wt in total) offered healing under both curing conditions before 28 days. The presence of NS assisted toward porosity refinement and NC increased the carbonates’ content. The newly formed material was dense, and its elemental analysis by SEM revealed the C-S-H compounds that were also verified by ATR.

Clay-based mortars are susceptible to water intake and exhibit low mechanical strength, presenting challenges in their application within the construction sector. This research addresses these vulnerabilities by investigating the combination of alkali activators with waterproofing agents, specifically a nano-clay and an acrylic emulsion, to enhance the properties of clay mortars. Alkali-activated materials are known for their superior mechanical properties and sustainable potential, especially when derived from low-cost by-products. Recent studies have focused on alkali activation using clays and soils as precursors to improve their physical and mechanical properties while increasing durability. However, the high absorbency of these mortars remains a concern, as it can lead to matrix degradation. Therefore, to address these problems, this research studied the combination of a highly alkaline activator (potassium metasilicate) with hydrophobic agents, such as a nano-clay and an acrylic emulsion, using two different clayey soils. The results indicated that potassium metasilicate (PO) enhanced the mechanical properties and stability for both aluminosilicate systems, while nano-clay (PONC) significantly reduced the capillary absorption through time, especially in A2 systems. The addition of acrylic emulsion (POD) proved highly effective in both systems, significantly improving durability. By integrating these agents, the mortar systems were protected against water intake, while durable construction materials were formed.

The present research lacks a thorough literature review, while overall no citations can be found in the manuscript. The subject of this research is a part of a wide topic with a great scientific interest; however, this paper lacks the analysis needed...