In this study, the effect of nanoparticle concentration was tested for both CuO and TiO₂ in eutectic mixture of sodium and potassium nitrate. Results showed an enhancement in specific heat capacity (C_p) for both types of nanoparticles (+10.48% at 440 °C for 0.1 wt % CuO and +4.95% at 440 °C for 0.5 wt % TiO₂) but the behavior toward a rise in concentration was different with CuO displaying its highest enhancement at the lowest concentration whilst TiO₂ showed no concentration dependence for three of the four different concentrations tested. The production of cluster of nanoparticles was visible in CuO but not in TiO₂. This formation of nanostructure in molten salt might promote the enhancement in C_p. However, the size and shape of these structures will most likely impact the energy density of the molten salt.

This paper proposes a power system concept that integrates photovoltaic (PV) and thermoelectric (TE) technologies to harvest solar energy from a wide spectral range. By introduction of the ‘spectrum beam splitting’ technique, short wavelength solar radiation is converted directly into electricity in the PV cells, while the long wavelength segment of the spectrum is used to produce moderate to high temperature thermal energy, which then generates electricity in the TE device. To overcome the intermittent nature of solar radiation, the system is also coupled to a thermal energy storage unit. A systematic analysis of the integrated system is carried out, encompassing the system configuration, material properties, thermal management, and energy storage aspects. We have also attempted to optimize the integrated system. The results indicate that the system configuration and optimization are the most important factors for high overall efficiency

In this study, TiO₂ nanoparticles (average particle size 16 nm) were successfully produced in molten salt phase and were showed to significantly enhance the specific heat capacity of a binary eutectic mixture of sodium and potassium nitrate (60/40) by 5.4 % at 390 °C and 7.5 % at 445 °C for 3.0 wt% of precursors used. The objective of this research was to develop a cost-effective alternate method of production which is potentially scalable, as current techniques utilized are not economically viable for large quantities. Enhancing the specific heat capacity of molten salt would promote more competitive pricing for electricity production by concentrating solar power plant. Here, a simple precursor (TiOSO₄) was added to a binary eutectic mixture of potassium and sodium nitrate, heated to 450 °C, and cooled to witness the production of nanoparticles.

Seeding nanoparticles in molten salts has been shown recently as a promising way to improve their thermo-physical properties. The prospect of such technology is of interest to both academic and industrial sectors in order to enhance the specific heat capacity of molten salt. The latter is used in concentrated solar power plants as both heat transfer fluid and sensible storage. This work explores the feasibility of producing and dispersing nanoparticles with a novel one pot synthesis method. Using such a method, CuO nanoparticles were produced in situ via the decomposition of copper sulphate pentahydrate in a KNO₃-NaNO₃ binary salt. Analyses of the results suggested preferential disposition of atoms around produced nanoparticles in the molten salt. Thermal characterization of the produced nano-salt suspension indicated the dependence of the specific heat enhancement on particle morphology and distribution within the salts.

This paper is focused on the characterisation and demonstration of Newtonian behaviour of salt at both high and low shear rate for sodium and potassium nitrate eutectic mixture (60/40) ranging from 250 °C to 500 °C. Analysis of published and experimental data was carried out to correlate all the numbers into one meaningful 4th order polynomial equation. Addition of a low amount of copper oxide nanoparticles to the mixture increased viscosity of 5.0%–18.0% compared to the latter equation.