Composite membranes of poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) or ethyl cellulose filled with magnetic nanoparticles, that is, ferroferric oxides (Fe₃O₄) were prepared. These membranes were examined for nitrogen and oxygen permeability. In the case of ethylcellulose membranes the gas flow was too high, since the macropore were formed. In further permeation measurements PPO membranes with 1 to 10 w/w% magnetic particles content were investigated. For the higher concentration of magnetite (more than 20%) in PPO polymer solution sedimentation phenomenon was observed. Mass transport coefficients (permeation and selectivity) were evaluated. Selectivity of the investigated membranes changed with the weight fraction of magnetic particles from oxygen (plain) towards nitrogen (2 and more w/w%).

Poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) and magnetic neodymium powder particles MQP-14-12 have been used for the preparation of magnetic mixed matrix membranes. Permeability diffusion and sorption coefficients of O₂, N₂, and synthetic air components were estimated for homogeneous and heterogeneous membranes using the Time Lag method based on dynamic experiments in a constant pressure system. The influence of magnetic field and magnetic powder particles on the gas transport properties of MMMs was studied. The results showed that the membrane permeation properties were improved with the magnetic neodymium particle filling. It was observed that the magnetic ethylcellulose and poly(2,6-dimethyl-1,4-phenylene oxide) membranes showed higher gas permeability, while their permselectivity and solubility were rather maintained or slightly increased. The results also showed that the magnetic powder addition enhanced gas diffusivity significantly in EC and PPO membranes.