Sulphur-doped carbon was synthesized using a thiophene-based twin monomer. While tetra(thiophene-2-ylmethoxy)-silane can be converted into sulphur containing nanocomposites, which lead to microporous sulphur-doped carbon, it is possible to produce additional mesopores by the use of templates. Thus, a variety of sulphur-doped carbon materials with tailored pore texture are available.

Natural fibers are a sustainable alternative to synthetic fibers due to their high weight‐specific Young's moduli and strengths. However, the mechanical properties of natural fibers are very sensitive to their moisture content. Therefore, chemical treatments are often applied to natural fibers to lower their water absorption and enhance fiber‐matrix interaction. The aim is to study the effects of fiber modifications with sodium hydroxide, silane, and siloxane on the water uptake and tensile properties of flax fiber composites produced via prepreg technology. In addition, the effect of moisture on the composites' tensile properties was investigated by conditioning one part of the tensile specimens according to DIN EN 2823 (at 70°C and 85% relative humidity). The NaOH treatment was the only modification that had positive effects on the Young's modulus and tensile strength in the unconditioned and conditioned state. The increase of the tensile modulus and strength are most likely due to changes in flax fiber composition, crystallinity of the cellulose and the rougher fiber surface of NaOH modified fibers. This shows that chemical treatment of natural fibers may improve the performance level of natural fiber composites and prevent a loss in their mechanical properties in humid environments.Highlights: Flax fiber modifications with sodium hydroxide, silane, and siloxane. Flax fiber composite production via prepreg technology. Water uptake after conditioning at 70°C and 85% relative humidity. Tensile tests before and after conditioning. SEM images of modified flax fibers.

Ground rubber from automobile tires is very difficult to recycle due to the cross-linking of the macromolecules and thus the lack of thermoplastic properties. The research consisted of assessing the processing possibility via the injection of highly filled PP/GTR compounds modified with 1.5 wt.% 2.5-dimethyl-2.5-di-(tert-butylperoxy)-hexane. GTR dosing ranged from 30 wt.% up to 90 wt.%. The evaluation of the processing properties of the obtained materials was carried out on the basis of the melt flow index test results and the signals recorded during processing by the injection molding by temperature and pressure sensors placed in the mold. The influence of the applied modifier on the changes in the mechanical properties of PP/GTR was determined with hardness, impact and static tensile tests. Moreover, thermal properties were obtained by the differential scanning calorimetry method. It has been found that it is possible to efficiently process compounds with high GTR content using injection molding. The presence of the filler allows to significantly reduce the cooling time in the injection mold and thus the time of the production cycle. It has been confirmed that 2.5-dimethyl-2.5-di-(tert-butylperoxy)-hexane modifies the rheological properties of PP and thus the PP/GTR composition. The lower viscosity of the matrix results in a more accurate bonding with the developed surface of the GTR grains, which results in better mechanical properties of the rubber-filled polypropylene.

Lightweight construction combines various materials to create resource efficient components. Thermoplastics (TPs) combined with polyurethane (PUR) foams are increasingly used to create hybrid composites. Optimizing the energy efficiency is one of the main issues in the development of production processes of components. Reducing the number of process steps offers great potential in this respect. PUR foam develops a strong adhesive bond with most materials. This is used for the manufacturing of hybrid composite components by filling complex cavities with PUR foam simultaneously bonded with other TP polymer components. This way, one process step for joining is saved. The interfaces in this composite structures are critical points of the failure. A huge variety of TP is used for the production of hybrid composite components and PUR foam develops varying bonding strengths with all of them. Selecting the suitable TPs for a durable bonding with PUR foam in the desired production process necessarily requires information about the respective specific adhesion. In this investigation, different TPs were processed with PUR foams in order to manufacture sandwich composites. The TP facings are produced in the injection moulding process. Subsequently, the facings are combined with the foam core during reaction injection moulding. The wetting behaviour was examined using the contact angle measurement and the mechanical strength of the interface in the sandwich composite was determined using a tensile test. A precise order of the selected TPs concerning their specific adhesion to PUR foams was achieved with these investigative methods.