In this study, 1,8-dioxo-octahydroxanthenes were prepared employing a simple, effective and environmentally sound approach utilizing an iron oxide nanocatalyst under solventless conditions. The proposed iron oxide nanomaterial exhibited high product yields, short reaction times and a facile work-up procedure. The synthesized catalyst was also found to be highly stable and reusable under the investigated conditions (up to twelve consecutive cycles) without any significant loss in its catalytic activity.

In this work, we report the incorporation of nickel oxide nanoparticles into a metal–organic framework (MOF) structure by a solvent-free mechanochemical strategy. In particular, the zirconium-based MOF UiO-66 was modified with different Ni loadings and characterized using complementary techniques including X-ray diffraction (XRD), N₂ porosimetry and X-ray photoelectron spectroscopy (XPS). The catalytic potential of the as-prepared Ni/UiO-66 materials in the hydrogenation reaction of methyl levulinate using 2-propanol as hydrogen donor solvent has been investigated under flow conditions. Under optimized conditions, the 5%Ni/UiO-66 led to the best catalytic performance (70% yield, 100% selectivity to gamma-valerolactone), which could be attributed to the higher content of the Ni species within the MOF structure. The obtained results are promising and contribute to highlighting the great potential of MOFs in biomass upgrading processes, opening the path to the sustainable development of the chemical industry.

In this study, the co-synthesis of TiO₂ and Cu metallic nanoparticles obtained via one-pot cost-efficient hydrothermal process has been addressed. Different nanocatalysts with Cu contents were characterized by X-ray diffraction, nitrogen porosimetry, scanning electron microscopy, and transmission electron microscopy. The TiO₂ and Cu metallic nanoparticles were synthesized with copper loading up to one (Cu/Ti atomic ratio). Synthesized catalysts exhibited pore sizes in the mesoporous range and high surface areas above 150 m²/g. The particle size for TiO₂ presented a homogeneous distribution of approximately 8 nm, moreover, Cu nanoparticles varied from 12 to >100 nm depending on the metal loading. The nanostructured materials were successfully tested in the conversion of trans-ferulic acid into vanillin under sustainable conditions, achieving the best performance for 0.3 Cu/Ti atomic ratio (70% vanillin yield).

A highly sustainable method for the preparation of supported iron oxide and copper nanoparticles (NPs) on a biomass-derived carbon by solvent-free mechanochemical process is reported. In-situ mechanochemically obtained extracts from orange peel could behave as a green reducing agent, allowing the formation of Cu metal nanoparticles as well as generating a magnetic phase (magnetite) in the systems via partial Fe³⁺ reduction. At the same time, orange peel residues also served as template and carbon source, adding oxygen functionalities, which were found to benefit the catalytic performance of mechanochemically synthesized nanomaterials. The series of magnetic Cu-Fe@OP were tested in the oxidation of trans-ferulic acid towards vanillin, remarkably revealing a maximum vanillin yield of 82% for the sample treated at 200 °C.

It has been brought to the attention of the Editorial Office that Figure 1 in the original publication