The geometry of a composite frusta-conical structure with 20 degrees apex angle was optimized using topology optimization method. The ATOM topology solver was used to perform optimization process. The structure was subjected to an axial compressive quasi-static loading where the criterion of optimization is the largest absorption of energy per unit volume. The optimization resulted in concave shell geometry with a volume reduction of 15%. To compare the effect of geometry on energy absorption capability, two types of GFRP specimen with different thickness were fabricated using filament winding and hand lay-up methods. The axial crushing test results were validated with numerical analysis using the commercial finite element software ABAQUS. The collapse mode and failure mechanism were investigated and identified. The presented methodology helps to find the better geometry instead of testing different geometries.

The present study investigates the effects of close-range blast loading of fibre metal laminates (FMLs) fabricated from woven glass polypropylene and aluminium alloy 2024-T3. The polypropylene layers and anodized aluminium are stacked in 3/2 layering configuration to investigate the impact energy absorbed through deformation and damage. In order to study the blast responses of FMLs, a 4-cable instrumented pendulum blast set-up is used. Effects of blast impulse and stand-off distance were examined. Investigation of the cross-section of FMLs are presented and damages such as fibre fracture, debonding, and global deformation are examined. Increasing stand-off distance from 4 to 14 mm resulted in a change of damage mode from highly localized perforation to global deformation.

This paper presents work on organically-modified montmorillonite (MMT) nanoclay embedded in rigid palm oil-based polyurethane (PU) foam. MMT was modified with organic surfactant diamino propane (DAP). PU foam was fabricated in closed mold, and the amount of DAP-MMT was varied in each foam formulation. The obtained foam was tested for its microstructure and morphology. Appearance of peaks from infra-red spectra corresponding to N-H, C=O, and C-N confirms the formation of PU networks. Scanning electron microscopy (SEM) revealed fine, closed-cellular structure at low clay loading; increasing DAP-MMT content induced larger cell sizes with blowholes. X-ray diffraction (XRD) indicates fully-exfoliated clays at 1 wt. % and partial-exfoliation at 3 wt. % clay loading, suggesting clumping of clays as DAP-MMT content increased.