In the field of metal matrix composites, it is a great challenge to improve the strength and elongation of magnesium matrix composites simultaneously. In this work, xTC4/AZ31 (x = 0.5, 1, 1.5 wt.%) composites were fabricated by spark plasma sintering (SPS) followed by hot extrusion. Scanning electron microscopy (SEM) showed that nano-TC4 (Ti-6Al-4V) was well dispersed in the AZ31 matrix. We studied the microstructure evolution and tensile properties of the composites, and analyzed the strengthening mechanism of nano-TC4 on magnesium matrix composites. The results showed that magnesium matrix composites with 1 wt.%TC4 had good comprehensive properties; compared with the AZ31 matrix, the yield strength (YS) was increased by 20.4%, from 162 MPa to 195 MPa; the ultimate tensile strength (UTS) was increased by 11.7%, from 274 MPa to 306 MPa, and the failure strain (FS) was increased by 21.1%, from 7.6% to 9.2%. The improvement in strength was mainly due to grain refinement and good interfacial bonding between nano-TC4 and the Mg matrix. The increase in elongation was the result of grain refinement and a weakened texture.

In this study, Ti particles reinforced Mg AZ31/Al 6082 composite sheets were successfully prepared by hot rolling, with the aim of revealing the effect of Ti particles addition on the mechanical behavior and microstructure of Mg AZ31/Al 6082 composite sheets. The results showed that Ti particles were uniformly distributed at the interface of the Mg/Al-Ti composite sheets, which could greatly reduce the amount of Mg-Al intermetallic compounds during annealing treatment. Compared to the Mg/Al sheet, the tensile strength and elongation of the Mg/Al-Ti sheet could be improved simultaneously after the annealing treatment. Ti particles addition hardly affected the grain size, texture type, and tensile fracture morphology of the Mg layer and Al layer in the composite sheets before and after annealing. This present study provides a new perspective on the mechanical behavior and microstructure of Mg/Al composites through the addition of metal particles.