Ferroalloys have become increasingly important due to their indispensable role in steelmaking. In addition, the demand for improved steel qualities has increased considerably, which in turn highlights the quality of ferroalloys. This is due to the fact that the impurities in ferroalloys directly and significantly influence the quality of steel products. To gain a better understanding of the main trace elements and inclusions in ferroalloys (such as FeSi, FeMn, SiMn, FeTi, FeCr, FeMo, FeNb, FeV, FeB, some complex ferroalloys) and their behaviours in steel melt after the additions of these ferroalloys, information from a large number of previous results on this topic was extensively reviewed in this work. The applications of different ferroalloys and their production trends were discussed. In addition, the effects of some trace element impurities from ferroalloys on the inclusion characteristics in steel were also discussed. The possible harmful inclusions in different ferroalloys were identified. Overall, the results showed that the inclusions present in ferroalloys had the following influence on the final steel cleanliness: (1) MnO, MnS and MnO–SiO₂–MnS inclusions from FeMn and SiMn alloys have a temporary influence on the steel quality; (2) the effect of large size SiO₂ inclusions (up to 200 μm) in FeSi and FeMo alloys on the steel cleanliness is not fully understood. The effect of Al, Ca contents should be considered before the addition of FeSi alloys. In addition, Al₂O₃ inclusions and relatively high Al content are commonly found in FeTi, FeNb and FeV alloys due to their production process. This information should be paid more attention to when these ferroalloys are added to steel; (3) except for the existing inclusions in these alloys, the Ti-rich, Nb-rich, V-rich carbides and nitrides, which have important effects on the steel properties also should be studied further; and (4) specific alloys containing REM oxides, Cr–C–N, Cr–Mn–O, Al₂O₃, Al–Ti–O, TiS and Ti(C, N) have not been studied enough to enable a judgement on their influence on the steel cleanliness. Finally, some suggestions were given for further studies for the development of ferroalloy productions.

The kinetic modeling for the nucleation, size growth, and compositional evolution of nonmetallic inclusions in steel was extensively reviewed in the present article. The nucleation and initial growth of inclusion in molten steel during deoxidation as well as the collision growth, motion, removal, and entrapment of inclusions in the molten steel in continuous casting (CC) tundish and strand were discussed. Moreover, the recent studies on the prediction of inclusion composition in CC semiproducts were introduced. Since the 1990s, the development of thermodynamic model and relevant databases for inclusion engineering has been initiated by the steel industry. Later, the commercial software FACTSAGE employing the FACT database was widely used to predict the gas (atmosphere/bubble)–liquid (steel/slag/inclusion)–solid (refractory/slag/steel/inclusion) multiphase equilibria. With the help of the comprehensive thermodynamic database and solution models in conjunction with the development of user-friendly computing packages, the kinetics of inclusion evolution in molten steel can be successfully predicted based on several kinetic models such as the coupled reaction (CR) model, reaction zone model, and tank series recirculation (TSR) model. However, some parameters are needed to represent the real processes according to the model employed at different operational or experimental conditions. The effect of reoxidation on the evolution of inclusions in the ladle and tundish, which was experimentally confirmed, can be simulated by the effective equilibrium reaction zone (EERZ) model. The complex slag–steel interfacial reaction phenomena have been successfully explained by the interfacial kinetic model based on the dynamic interfacial tension and oxygen adsorption/desorption characteristics at the slag-steel interface.