Poly(methyl methacralyate) (PMMA) has long been used in dentistry as a base polymer for dentures, and it is recently being used for the 3D printing of dental materials. Despite its many advantages, its susceptibility to microbial colonization remains to be overcome. In this study, the interface between 3D-printed PMMA specimens and oral salivary biofilm was studied following the addition of zwitterionic materials, 2-methacryloyloxyethyl phosphorylcholine (MPC) or sulfobetaine methacrylate (SB). A significant reduction in bacterial and biofilm adhesions was observed following the addition of MPC or SB, owing to their protein-repellent properties, and there were no significant differences between the two test materials. Although the mechanical properties of the tested materials were degraded, the statistical value of the reduction was minimal and all the properties fulfilled the requirements set by the International Standard, ISO 20795-2. Additionally, both the test materials maintained their resistance to biofilm when subjected to hydrothermal fatigue, with no further deterioration of the mechanical properties. Thus, novel 3D-printable PMMA incorporated with MPC or SB shows durable oral salivary biofilm resistance with maintenance of the physical and mechanical properties.

Herein we evaluate the effect of nanodiamond (ND) incorporation on the mechanical properties of poly(methyl methacrylate) (PMMA) nanocomposite. Three quantities of ND (0.1, 0.3, and 0.5 wt.%) were tested against the control and zirconium oxide nanoparticles (ZrO). Flexural strength and elastic modulus were measured using a three-point bending test, surface hardness was evaluated using the Vickers hardness test, and surface roughness was evaluated using atomic force microscopy (AFM), while fungal adhesion and viability were studied using Candida albicans. Samples were also analyzed for biofilm thickness and biomass in a saliva-derived biofilm model. All groups of ND-PMMA nanocomposites had significantly greater mean flexural strengths and statistically improved elastic modulus, compared to the control and ZrO groups (P < 0.001). The Vickers hardness values significantly increased compared to the control group (P < 0.001) with 0.3% and 0.5% ND. ND addition also gave significant reduction in fungal adhesion and viability (P < 0.001) compared to the control group. Finally, salivary biofilm formation was markedly reduced compared to the ZrO group. Hence, the incorporation of 0.1–0.5 wt.% ND with auto- polymerized PMMA resin significantly improved the flexural strength, elastic modulus, and surface hardness, and provided considerable fungal resistance.

Calcium silicate-based cements (CSCs) are commonly used for endodontic procedures; however, their antibacterial effects are limited. The objective of this study was to develop a 2-methacryloyloxyethyl phosphorylcholine (MPC)-incorporated CSC with improved antibacterial properties, while maintaining the original advantageous features of CSC. MPC was incorporated into a commercial CSC (Endocem MTA) at 0 wt% (control), 1.5%, 3.0 wt%, 5.0 wt%, 7.5 wt%, and 10 wt%. The setting time, compressive strength, water sorption, and glycerol contact angle were measured. Protein absorption was measured and bacterial adhesion on the surface was evaluated using Enterococcus faecalis. The bactericidal effect was examined by the disc diffusion test. Mineralization ability was assessed based on calcium ion deposition, as assessed by alizarin red staining, after immersion into Hank’s balanced salt solution for 7 days. High concentrations of MPC in CSC (7.5 wt% and 10 wt%) increased the setting time, reduced compressive strength, and reduced wettability. MPC (3 wt%) had greater protein repellent and anti-biofouling effects than those of control and test materials (P < 0.001). However, no bactericidal effect was observed for any control or test materials. There was greater calcium ion deposition on the surface of MPC-supplemented CSC than on the control (P < 0.001). The addition of 3 wt% MPC polymer to CSC confers protein-repellent properties and reduced bacterial attachment, with the potential for improved mineralization.