Wireless sensor networks usually rely on internal permanent or rechargeable batteries as a power supply, causing high maintenance efforts. An alternative solution is to supply the entire system by harvesting the ambient energy, for example, by transducing ambient vibrations into electric energy by virtue of the piezoelectric effect. The purpose of this paper is to present a simple engineering approach for the bandwidth optimization of vibration energy harvesting systems comprising multiple piezoelectric cantilevers (PECs). The frequency tuning of a particular cantilever is achieved by changing the tip mass. It is shown that the bandwidth enhancement by mass tuning is limited and requires several PECs with close resonance frequencies. At a fixed frequency detuning between subsequent PECs, the achievable bandwidth shows a saturation behavior as a function of the number of cantilevers used. Since the resonance frequency of each PEC is different, the output voltages at a particular excitation frequency have different amplitudes and phases. A simple power-transfer circuit where several PECs with an individual full wave bridge rectifier are connected in parallel allows one to extract the electrical power close to the theoretical maximum excluding the diode losses. The experiments performed on two- and three-PEC arrays show reasonable agreement with simulations and demonstrate that this power-transfer circuit additionally influences the frequency dependence of the harvested electrical power.

Elongations of magnetoactive elastomers (MAEs) under ascending–descending uniform magnetic fields were studied experimentally using a laboratory apparatus specifically designed to measure large extensional strains (up to 20%) in compliant MAEs. In the literature, such a phenomenon is usually denoted as giant magnetostriction. The synthesized cylindrical MAE samples were based on polydimethylsiloxane matrices filled with micrometer-sized particles of carbonyl iron. The impact of both the macroscopic shape factor of the samples and their magneto-mechanical characteristics were evaluated. For this purpose, the aspect ratio of the MAE cylindrical samples, the concentration of magnetic particles in MAEs and the effective shear modulus were systematically varied. It was shown that the magnetically induced elongation of MAE cylinders in the maximum magnetic field of about 400 kA/m, applied along the cylinder axis, grew with the increasing aspect ratio. The effect of the sample composition is discussed in terms of magnetic filler rearrangements in magnetic fields and the observed experimental tendencies are rationalized by simple theoretical estimates. The obtained results can be used for the design of new smart materials with magnetic-field-controlled deformation properties, e.g., for soft robotics.

Recently, highly sensitive magnetic field sensors using the magnetoelectric effect in composite ferromagnetic-piezoelectric layered structures have been demonstrated. However, most of the proposed concepts are not useful for measuring dc magnetic fields, because the conductivity of piezoelectric layers results in a strong decline of the sensor’s sensitivity at low frequencies. In this paper, a novel functional principle of magnetoelectric sensors for dc magnetic field measurements is described. The sensor employs the nonlinear effect of voltage harmonic generation in a composite magnetoelectric structure under the simultaneous influence of a strong imposed ac magnetic field and a weak dc magnetic field to be measured. This physical effect arises due to the nonlinear dependence of the magnetostriction in the ferromagnetic layer on the magnetic field. A sensor prototype comprising of a piezoelectric fibre transducer sandwiched between two layers of the amorphous ferromagnetic Metglas ^® alloy was fabricated. The specifications regarding the magnetic field range, frequency characteristics, and noise level were studied experimentally. The prototype showed the responsivity of 2.5 V mT ⁻¹ and permitted the measurement of dc magnetic fields in the range of ~10 nT to about 0.4 mT. Although sensor operation is based on the nonlinear effect, the sensor response can be made linear with respect to the measured magnetic field in a broad dynamic range extending over 5 orders of magnitude. The underlying physics is explained through a simplified theory for the proposed sensor. The functionality, differences and advantages of the magnetoelectric sensor compare well with fluxgate magnetometers. The ways to enhance the sensor performance are considered.

The dependence of the resonant direct magnetoelectric effect on temperature is studied experimentally in planar composite structures. Samples of rectangular shapes with dimensions of 5 mm × 20 mm employed ferromagnetic layers of either an amorphous (metallic glass) alloy or nickel with a thickness of 20–200 μm and piezoelectric layers of single crystalline langatate material or lead zirconate titanate piezoelectric ceramics with a thickness of 500 μm. The temperature of the samples was varied in a range between 120 and 390 K by blowing a gaseous nitrogen stream around them. It is shown that the effective characteristics of the magnetoelectric effect—such as the mechanical resonance frequency f_r, the quality factor Q and the magnitude of the magnetoelectric coefficient α_E at the resonance frequency—are contingent on temperature. The interrelations between the temperature changes of the characteristics of the magnetoelectric effect and the temperature variations of the following material parameters—Young’s modulus Y, the acoustic quality factor of individual layers, the dielectric constant ε, the piezoelectric modulus d of the piezoelectric layer as well as the piezomagnetic coefficients λ⁽ⁿ⁾ of the ferromagnetic layer—are established. The effect of temperature on the characteristics of the nonlinear magnetoelectric effect is observed for the first time. The results can be useful for designing magnetoelectric heterostructures with specified temperature characteristics, in particular, for the development of thermally stabilized magnetoelectric devices.

The magnetoelectric (ME) effect is studied in composite two- and three-layer disk structures containing magnetostriction layers of an amorphous FeNiSiC ferromagnet and a lead zirconate titanate piezoelectric layer. Due to a high magnetostriction (∼33 × 10⁻⁶) and a low saturation field (∼200 Oe), an FeNiSiC layer has a high piezomagentic coefficient, which results in an effective ME coupling in low fields (∼25 Oe). The ME effect is ∼0.2 V cm⁻¹ Oe⁻¹ at a low frequency and increases to 11.9 and 13.2 V cm⁻¹ Oe⁻¹ when bending and in-plane mechanical vibrations are excited in a resonance manner in the structures at frequencies of ∼8.2 and ∼170.0 kHz, respectively. Structures containing amorphous FeNiSiC layers are promising for magnetic field transducers and electric energy generators and converters.

This paper investigates the possibilities of creating magnetic field sensors using the direct magnetoelectric (ME) effect in a monolithic heterostructure of amorphous ferromagnetic material/langatate. Layers of 1.5 μm-thick FeCoSiB amorphous ferromagnetic material were deposited on the surface of the langatate single crystal using magnetron sputtering. At the resonance frequency of the structure, 107 kHz, the ME coefficient of linear conversion of 76.6 V/(Oe∙cm) was obtained. Furthermore, the nonlinear ME effect of voltage harmonic generation was observed with an increasing excitation magnetic field. The efficiency of generating the second and third harmonics was about 6.3 V/(Oe²∙cm) and 1.8 V/(Oe³∙cm), respectively. A hysteresis dependence of ME voltage on a permanent magnetic field was observed due to the presence of α-Fe iron crystalline phases in the magnetic layer. At the resonance frequency, the monolithic heterostructure had a sensitivity to the AC magnetic field of 4.6 V/Oe, a minimum detectable magnetic field of ~70 pT, and a low level of magnetic noise of 0.36 pT/Hz^1/2, which allows it to be used in ME magnetic field sensors.