The additive of few-layer and rod-like MXene shows great effect on improving the mechanical property and electrochemical performance of Ni-rich LiNi _0.8 Co _0.1 Mn _0.1 cathode.

Two kinds of cotton fiber based magnetic carbon microtubes (PCMT/Co and CMT/Co) have demonstrated great potential for application in the field of electromagnetic wave absorption.

Conductive and degradable nanofibrous scaffolds have great potential in promoting cell growth, proliferation, and differentiation under an external electric field. Although the issue of inferior electrical conductivity in body fluids still exists, polyaniline (PANI)-based degradable nanofibers can promote cell adhesion, growth, and proliferation. To investigate whether the effect is caused by the PANI morphology, we selected three inorganic acids as dopants in the process of PANI in situ oxidative polymerization: hydrochloric acid, sulfuric acid, and perchloric acid. The obtained polyaniline/polylactic acid (PANI/PLA) composite nanofibers were characterized via SEM, FTIR, and XPS analysis, and we confirmed that the PLA nanofibers were successfully coated by PANI without any change to the porous structure of the PLA nanofibers. The in vitro mechanical properties and degradability indicated that the oxidation of acid dopants should be considered and that it was likely to have a higher oxidation degradation effect on PLA nanofibers. The contact angle test demonstrated that PANI/PLA composite nanofibers with different surface morphologies have good wettability, implying that they meet the requirements of bone tissue engineering scaffolds. The surface roughness and cell viability demonstrated that different PANI morphologies on the surface can promote cell proliferation. The higher the surface roughness of the PANI, the better the biocompatibility. Consequently, the regulated surface morphology of PANI/PLA composite nanofibers via different acids doping has positive effect on biocompatibility in tissue engineering.

In this work, a few-layer MXene is prepared and sprinkled on a commercial polypropylene (PP) separator by a facile spraying method to enhance the electrochemistry of the Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) cathode. Scanning electron microscope (SEM) and X-ray diffraction (XRD) are used to characterize the morphology and structure of MXene. Fourier transform infrared spectroscopy (FT-IR) and a contact angle tester are used to measure the bond structure and surface wettability PP and MXene/PP separator. The effect of the MXene/PP separator on the electrochemical performance of ternary NCM811 material is tested by an electrochemical workstation. The results show that the two-dimensional MXene material could improve the wettability of the separator to the electrolyte and greatly enhance the electrochemical properties of the NCM811 cathode. During 0.5 C current density cycling, the Li/NCM811 cell with MXene/PP separator remains at 166.2 mAh/g after the 100 cycles with ~90.7% retention. The R_ct of MXene/PP cell is measured to be ~28.0 Ω. Combining all analyses results related to MXene/PP separator, the strategy by spraying the MXene on commercial PP is considered as a simple, convenient, and effective way to improve the electrochemical performance of the Ni-rich NCM811 cathode and it is expected to achieve large-scale in high-performance lithium-ion batteries in the near future.