This review paper examines the current state-of-the-art in fabrication of aligned fibers via electrospinning techniques and the effects of these techniques on the mechanical and dielectric properties of electrospun fibers. Molecular orientation, system configuration to align fibers, and post-drawing treatment, like hot/cold drawing process, contribute to better specific strength and specific stiffness properties of nanofibers. The authors suggest that these improved, aligned nanofibers, when applied in composites, have better mechanical and dielectric properties for many structural and multifunctional applications, including advanced aerospace applications and energy storage devices. For these applications, most fiber alignment electrospinning research has focused on either mechanical property improvement or dielectric property improvement alone, but not both simultaneously. Relative to many other nanofiber formation techniques, the electrospinning technique exhibits superior nanofiber formation when considering cost and manufacturing complexity for many situations. Even though the dielectric property of pure nanofiber mat may not be of general interest, the analysis of the combined effect of mechanical and dielectric properties is relevant to the present analysis of improved and aligned nanofibers. A plethora of nanofibers, in particular, polyacrylonitrile (PAN) electrospun nanofibers, are discussed for their mechanical and dielectric properties. In addition, other types of electrospun nanofibers are explored for their mechanical and dielectric properties. An exploratory study by the author demonstrates the relationship between mechanical and dielectric properties for specimens obtained from a rotating mandrel horizontal setup.

Fused filament fabrication (FFF) is one of the most popular additive manufacturing (AM) techniques used to fabricate polymeric structures. However, these polymeric structures suffer from an inherent deficiency of weak inter-laminar tensile strength. Because of this weak inter-laminar strength, these parts fail prematurely and exhibit only a fraction of the mechanical properties of those fabricated using conventional means. In this paper, we study the effect of thermal annealing in the presence of an initially applied static uniaxial load on the ultimate tensile strength of parts fabricated using FFF. Tensile specimens or dogbones were fabricated from an acrylonitrile butadiene styrene (ABS) filament with a glass transition temperature (T_g) of 105 °C; these specimens were then isothermally annealed, post manufacture, in a fixture across a given range of temperatures and static loads. Tensile testing was then performed on these specimens to gauge the effect of the thermal annealing and static loading on inter-laminar tensile strength by measuring the ultimate tensile strength of the specimens. A design of experiments (DOE) approach was followed to calculate the main and interaction effects of the two factors (temperature and static loading) on the ultimate tensile strength, and an analysis of variance was conducted. Cross-sectional images of the specimens were studied to observe the changes in the mesostructure of the specimens that led to the increase in inter-laminar strength of the parts. The results show that temperature plays a dominant role in increasing the ultimate tensile strength and an 89% increase in the average ultimate tensile strength was seen corresponding to an annealing temperature of 160 °C. A change in the mesostructure of the parts is seen, which is characterized by an increase in bond length and void coalescence. These results can be helpful in studying the structural strength of 3D printed parts, and thus could eventually guide the fabrication of components with strength comparable to those of conventional manufacturing techniques.

This paper deals with the dielectric and mechanical characterizations of polyacrylonitrile (PAN)-aligned electrospun nanofiber mats. A two factor three level full factorial experiment is conducted to understand the effect of various parameters on dielectric and mechanical responses. These responses are recorded against randomly oriented and aligned nanofiber mats. Improved properties of electrospun mats have applications in the field of energy storage and nanocomposite reinforcement. Dielectric and mechanical characterizations of PAN mats are vital, as the aligned electrospun mats were found to be useful in advanced energy and mechanical reinforcement applications. Therefore, it is paramount to understand the effects of system parameters to these properties. The design of experiment (DoE) includes two factors and three level full factorial experiments with concentrations of PAN solutions at 8 wt.%, 9 wt.%, and 10 wt.%, and speed of the rotating mandrel (collector) at 3 volt (V), 4 V, and 5 V inputs. The electric field intensity used in the experiment is 1 kV/cm. DoE is conducted to understand the nonlinear interactions of parameters to these responses. The dielectric and mechanical characterizations of 8 wt.%, 9 wt.%, and 10 wt.% with different speeds for the original and improved systems are discussed. It was observed that at 9 wt.% and at all mandrel speeds, the dielectric and tensile properties are optimum.