Hydrogen-induced disproportionation (HID) during the cycles of absorption and desorption leads to a serious decline in the storage capacity of the ZrCo alloy, which has been recognized as the biggest obstacle to its application. Therefore, the prerequisite of a ZrCo application is to solve its anti-disproportionation problem in the field of rapid hydrogen isotope storage. Beyond surface modification and nanoball milling, this work systematically reviews the method of element substitution, which can obviously improve the anti-disproportionation. From a micro angle, as hydrogen atoms that occupy the 8e site in the ZrCoH₃ lattice are instable and are considered to be the driving force of disproportionation, researchers believe that element substitution by changing the occupation of hydrogen atoms at the 8e site can improve the anti-disproportionation of the alloy. At present, Ti/Nb substitutions for the Zr terminal among substitute elements have an excellent anti-disproportionation performance. In this work, up-to-date research studies on anti-disproportionation and its disproportionation mechanism of the ZrCo alloy are introduced by combining experiments and simulations. Moreover, the optimization of the alloy based on the occupation mechanism of 8e sites is expected to improve the anti-disproportionation of the ZrCo alloy.

U-Mo alloys were considered to be the most promising candidates for high-density nuclear fuel. The uniaxial tensile behavior of nanocrystalline U-10Mo alloys with average grain sizes of 8–23 nm was systematically studied by molecular dynamics (MD) simulation, mainly focusing on the influence of average grain size on the mechanical properties and deformation mechanisms. The results show that Young’s modulus, yield strength and ultimate tensile strength follow as average grain size increases. During the deformation process, localized phase transitions were observed in samples. Grain boundary sliding and grain rotation, as well as twinning, dominated the deformation in the smaller and larger grain sizes samples, respectively. Increased grain size led to greater localized shear deformation, resulting in greater stress drop. Additionally, we elucidated the effects of temperature and strain rate on tensile behavior and found that lower temperatures and higher strain rates not only facilitated the twinning tendency but also favored the occurrence of phase transitions in samples. Results from this research could provide guidance for the design and optimization of U-10Mo alloys materials.