The oxygen evolution reaction is the bottleneck to energy-efficient water-based electrolysis for the production of hydrogen and other solar fuels. In proton exchange membrane water electrolysis (PEMWE), precious metals have generally been necessary for the stable catalysis of this reaction. In this work, we report that delamination of cobalt tungstate enables high activity and durability through the stabilization of oxide and water-hydroxide networks of the lattice defects in acid. The resulting catalysts achieve lower overpotentials, a current density of 1.8 amperes per square centimeter at 2 volts, and stable operation up to 1 ampere per square centimeter in a PEMWE system at industrial conditions (80°C) at 1.77 volts; a threefold improvement in activity; and stable operation at 1 ampere per square centimeter over the course of 600 hours.

Electrocatalytic organic compound oxidation reactions (OCORs) have been intensively studied for energy and environmentally benign applications. However, relatively little effort has been devoted to developing a fundamental understanding of OCORs, including the detailed competition with side reactions and activity limitations, thus inhibiting the rational design of high-performance electrocatalysts. Herein, by taking the NiWO₄-catalysed urea oxidation reaction (UOR) in aqueous media as an example, the competition between the OCOR and the oxygen evolution reaction (OER) within a wide potential range is examined. It is shown that the root of the competition can be ascribed to insufficient surface concentration of dynamic Ni³⁺, an active site shared by both the UOR and OER. A similar phenomenon is observed in other OCOR electrocatalysts and systems. To address the issue, a “controllable reconstruction of pseudo-crystalline bimetal oxides” design strategy is proposed to maximise the dynamic Ni³⁺ population and manipulate the competition between the UOR and the OER. The optimised electrocatalyst delivers best-in-class performance and an ∼10-fold increase in current density at 1.6 V versus the reversible hydrogen electrode for alkaline urea electrolysis compared to those of the pristine materials.

Understanding the effect of noncovalent interactions of intermediates at the polarized catalyst-electrolyte interface on water oxidation kinetics is key for designing more active and stable electrocatalysts. Here, we combine operando optical spectroscopy, X-ray absorption spectroscopy (XAS), and surface-enhanced infrared absorption spectroscopy (SEIRAS) to probe the effect of noncovalent interactions on the oxygen evolution reaction (OER) activity of IrO_x in acidic and alkaline electrolytes. Our results suggest that the active species for the OER (Ir^4.x+-*O) binds much stronger in alkaline compared with acid at low coverage, while the repulsive interactions between these species are higher in alkaline electrolytes. These differences are attributed to the larger fraction of water within the cation hydration shell at the interface in alkaline electrolytes compared to acidic electrolytes, which can stabilize oxygenated intermediates and facilitate long-range interactions between them. Quantitative analysis of the state energetics shows that although the *O intermediates bind more strongly than optimal in alkaline electrolytes, the larger repulsive interaction between them results in a significant weakening of *O binding with increasing coverage, leading to similar energetics of active states in acid and alkaline at OER-relevant potentials. By directly probing the electrochemical interface with complementary spectroscopic techniques, our work goes beyond conventional computational descriptors of the OER activity to explain the experimentally observed OER kinetics of IrO_x in acidic and alkaline electrolytes.

The production of green hydrogen in water electrolyzers is limited by the oxygen evolution reaction (OER). State-of-the-art electrocatalysts are based on Ir. Ru electrocatalysts are a suitable alternative provided their performance is improved. Here we show that low-Ru-content pyrochlores (R₂MnRuO₇, R = Y, Tb and Dy) display high activity and durability for the OER in acidic media. Y₂MnRuO₇ is the most stable catalyst, displaying 1.5 V at 10 mA cm⁻² for 40 h, or 5000 cycles up to 1.7 V. Computational and experimental results show that the high performance is owed to Ru sites embedded in RuMnO_x surface layers. A water electrolyser with Y₂MnRuO₇ (with only 0.2 mg_Ru cm⁻²) reaches 1 A cm⁻² at 1.75 V, remaining stable at 200 mA cm⁻² for more than 24 h. These results encourage further investigation on Ru catalysts in which a partial replacement of Ru by inexpensive cations can enhance the OER performance.

This report describes a method to fabricate high-surface-area boron-doped diamond (BDD) electrodes using so-called ‘black silicon’ (bSi) as a substrate. This is a synthetic nanostructured material that contains high-aspect-ratio nano-protrusions, such as spikes or needles, on the Si surface produced via plasma etching. We now show that coating a bSi surface composed of 15 μm-high needles conformably with BDD produces a robust electrochemical electrode with high sensitivity and high electroactive area. A clinically relevant demonstration of the efficacy of these electrodes is shown by measuring their sensitivity for detection of dopamine (DA) in the presence of an excess of uric acid (UA). Finally, the nanostructured surface of bSi has recently been found to generate a mechanical bactericidal effect, killing both Gram-negative and Gram-positive bacteria at high rates. We will show that BDD-coated bSi also acts as an effective antibacterial surface, with the added advantage that being diamond-coated it is far more robust and less likely to become damaged than Si.