As lightweight design gains more and more attention, time and cost-efficient joining methods such as clinching are becoming more popular. A clinch point’s quality is usually determined by ex situ destructive analyses such as microsectioning. However, these methods do not yield the detection of phenomena occurring during loading such as elastic deformations and cracks that close after unloading. Alternatively, in situ computed tomography (in situ CT) can be used to investigate the loading process of clinch points. In this paper, a method for in situ CT analysis of a single-lap shear test with clinched metal sheets is presented at the example of a clinched joint with two 2 mm thick aluminum sheets. Furthermore, the potential of this method to validate numerical simulations is shown. Since the sheets’ surfaces are locally in contact with each other, the interface between both aluminum sheets and therefore the exact contour of the joining partners is difficult to identify in CT analyses. To compensate for this, the application of copper varnish between the sheets is investigated. The best in situ CT results are achieved with both sheets treated. It showed that with this treatment, in situ CT is suitable to properly observe the three-dimensional deformation behavior and to identify the failure modes.

Recent developments in automotive and aircraft industry towards a multi-material design pose challenges for modern joining technologies due to different mechanical properties and material compositions of various materials such as composites and metals. Therefore, mechanical joining technologies like clinching are in the focus of current research activities. For multi-material joints of metals and thermoplastic composites thermally assisted clinching processes with advanced tool concepts are well developed. The material-specific properties of fibre-reinforced thermoplastics have a significant influence on the joining process and the resulting material structure in the joining zone. For this reason, it is important to investigate these influences in detail and to understand the phenomena occurring during the joining process. Additionally, this provides the basis for a validation of a numerical simulation of such joining processes. In this paper, the material structure in a joint resulting from a thermally assisted clinching process is investigated. The joining partners are an aluminium sheet and a thermoplastic composite (organo sheet). Using computed tomography enables a three-dimensional investigation that allows a detailed analysis of the phenomena in different joining stages and in the material structure of the finished joint. Consequently, this study provides a more detailed understanding of the material behavior of thermoplastic composites during thermally assisted clinching.

In lightweight design, clinching is a cost-efficient solution as the joint is created through localized cold-forming of the joining parts. A clinch point’s quality is usually assessed using ex-situ destructive testing methods. These, however, are unable to detect phenomena immediately during the joining process. For instance, elastic deformations reverse and cracks close after unloading. In-situ methods such as the force-displacement evaluation are used to control a clinching process, though deviations in the clinch point geometry cannot be derived with this method. To overcome these limitations, the clinching process can be investigated using in-situ computed tomography (in-situ CT). However, a clinching tool made of steel would cause strong artefacts and a high attenuation in the CT measurement, reducing the significance of this method. Additionally, when joining parts of the same material, the sheet-sheet interface is hardly detectable. This work aims at identifying, firstly, tool materials that allow artefact-reduced CT measurements during clinching, and, secondly, radiopaque materials that can be applied between the joining parts to enhance the detectability of the sheet-sheet interface. Therefore, both CT-suitable tool materials and radiopaque materials are selected and experimentally investigated. In the clinching process, two aluminium sheets with radiopaque material in between are clinched in a single-step (rotationally symmetric joint without cut section). It is shown that e.g. silicon nitride is suited as tool material and a tin layer is suitable to enhance the detectability of the sheet-sheet interface.