This article examines the process for the synthesis of forsterite–spinel (2MgO·SiO₂/MgO·Al₂O₃) refractory ceramics from fly ash and alumina as sources of aluminum oxide. Raw materials were milled, mixed in different ratios and sintered at 1500 °C for 2 h. Sintered samples were characterized by XRD, thermal analyses and SEM. Porosity, water absorption, bulk density, refractoriness, refractoriness under load and thermal shock resistance were also investigated. The impact of fly ash as a raw material was investigated in accordance with the resulting properties and microstructure of samples with fly ash and alumina as the raw materials. Due to the positive effect of flux oxides (iron oxides and alkalis) on sintering, the mullite contained in fly ash completely decomposed into silica and alumina, which, together with magnesium oxide, formed spinel. This led to improved microstructural and mechanical properties and thermal shock resistance. In particular, mixtures with 10 wt.% and 20 wt.% of fly ash had the most promising results compared to alumina mixtures. Both modulus of rupture and thermal shock resistance were improved, while the impact on refractory properties was minimal. The novelty of this research lies in the recycling of fly ash, a by-product from coal-burning power plants, into a raw material for the production of forsterite–spinel refractory ceramics.

In this study, the potential use of waste diatomaceous earth from the production of diatomaceous earth for filtration purposes, as an alternative raw material for foam glass production, was explored. The chemical and mineralogical composition and the high temperature behavior of waste diatomite were studied to assess its suitability for foam glass production. Glass-ceramic foams were prepared using NaOH solution as a foaming agent, via a hydrate mechanism. The influence of different pretreatments and firing temperatures on the foam’s structure, bulk density and compressive strength was investigated. High temperature behavior was studied using TG/DTA analysis and high temperature microscopy. Phase composition was studied using X-ray diffraction analysis. Glass-ceramic foam samples of a high porosity comparable to conventional foam glass products were fabricated. The pretreatment temperature, foaming temperature and sintering holding time were found to have a significant influence on foam properties. With increased pretreatment temperature, pyrogenic carbon from the thermal decomposition of organic matter contained in the raw material acted as an additional foaming agent and remained partially unoxidized in prepared foams. The bulk densities of prepared samples ranged from 150 kg/m³ to 510 kg/m³ and their compressive strengths were between 140 and 1270 kPa.

This article aims to investigate the corrosion resistance of novel fly ash–based forsterite–spinel (Mg₂SiO₄-MgAl₂O₄) refractory ceramics to various corrosive media in comparison with reactive alumina–based ceramics. Because fly ash is produced in enormous quantities as a byproduct of coal-burning power stations, it could be utilized as an affordable source of aluminum oxide and silicon oxide. Corrosion resistance to iron, clinker, alumina, and copper was observed by scanning electron microscope with an elemental probe. The influence on the properties after firing was also investigated. Fly ash–based and reactive alumina–based mixtures were designed to contain 10%, 15% and 20% of spinel after firing. Raw material mixtures were sintered at 1550 °C for two hours. X-ray diffraction analysis and scanning electron microscopy were used to analyze sintered samples. The apparent porosity, bulk density, modulus of rupture, and refractory and thermo–mechanical properties were also investigated. The experimental results disclosed that the modulus of rupture, thermal shock resistance and microstructure were improved with increasing amounts of spinel in the fired samples. An analysis of the transition zones between corrosive media and ceramics revealed that all mixtures have good resistance against corrosion to iron, clinker, aluminum and copper.

The properties of different Czech fluidized fly ashes FFA (class C fly ash according to ASTM C618 12a with high content of CaO in the form of anhydrite primarily) and emisions of SO2 in flue gas during the firing of FFA are discussed. The decomposition of anhydrite CaSO4 was observed during the soaking time at 1200 °C during the firing of dry pressed bodies based on pure fluidized fly ash. The effect od fluidized fly ashes admixtures on the properties of ceramic bodies is as fluxing agent and the source of CaO for the creation of anorthite in the fired ceramic body. The properties of domestic fluidized fly ashes in connection with their utilization in ceramic technology are described.