Tensile strength is an important material property for rocks. In applications where rocks are subjected to dynamic loads, the dynamic tensile strength is the controlling parameter. Similar to the study of static tensile strength, there are various methods proposed to measure the dynamic tensile strength of rocks. Here we examine dynamic tensile strength values of Laurentian granite (LG) measured from three methods: dynamic direct tension, dynamic Brazilian disc (BD) test, and dynamic semi-circular bending (SCB). We found that the dynamic tensile strength from direct tension has the lowest value, and the dynamic SCB gives the highest strength at a given loading rate. Because the dynamic direct tension measures the intrinsic rock tensile strength, it is thus necessary to reconcile the differences in strength values between the direct tension and the other two methods. We attribute the difference between the dynamic BD results and the direct tension results to the overload and internal friction in BD tests. The difference between the dynamic SCB results and the direct tension results can be understood by invoking the non-local failure theory. It is shown that, after appropriate corrections, the dynamic tensile strengths from the two other tests can be reduced to those from direct tension

Incorporating masks into building materials offers a potential solution to the environmental threat of disposable masks with promising material performance. However, research on their dynamic properties is lacking to further determine the application range of the new composite. This study addresses this gap by shredding face masks into strips and incorporating them into mortars at varying volume ratios. The integrity and compactness of the mortar was measured and characterized by P-wave velocity, while dynamic compression properties were explored using a split Hopkinson pressure bar (SHPB) system. Subsequently, sieve analysis was conducted on the fractured specimens. The results indicate that incorporating masks generally improves the mortar integrity and the fragmentation after impacting. The dynamic uniaxial compression strength (DUCS) decreased for all mixing designs compared to plain ones under a constant loading rate. Meanwhile, the dissipated energy density showed a similar trend to the P-wave velocity, exhibiting less pronounced enhancement at higher loading rates. According to the dynamic characteristics, a dynamic constitutive model based on the Lemaitre principle and Weibull distribution of damage is developed and validated. The test results are further understood through the perspective of the mechanism of mask inclusion.