In this study, a series of bio-based thermoplastic polyurethane (TPU) was synthesized via the solvent-free one-shot method using 100% bio-based polyether polyol, prepared from fermented corn, and 1,4-butanediol (BDO) as a chain extender. The average molecular weight, degree of phase separation, thermal and mechanical properties of the TPU-based aromatic (4,4-methylene diphenyl diisocyanate: MDI), and aliphatic (bis(4-isocyanatocyclohexyl) methane: H₁₂MDI) isocyanates were investigated by gel permeation chromatography, Fourier transform infrared spectroscopy, atomic force microscopy, X-ray Diffraction, differential scanning calorimetry, dynamic mechanical thermal analysis, and thermogravimetric analysis. Four types of micro-phase separation forms of a hard segment (HS) and soft segment (SS) were suggested according to the [NCO]/[OH] molar ratio and isocyanate type. The results showed (a) phase-mixed disassociated structure between HS and SS, (b) hydrogen-bonded structure of phase-separated between HS and SS forming one-sided hard domains, (c) hydrogen-bonded structure of phase-mixed between HS, and SS and (d) hydrogen-bonded structure of phase-separated between HS and SS forming dispersed hard domains. These phase micro-structure models could be matched with each bio-based TPU sample. Accordingly, H-BDO-2.0, M-BDO-2.0, H-BDO-2.5, and M-BDO-3.0 could be related to the (a)—form, (b)—form, (c)—form, and (d)—form, respectively.

Bio-based thermoplastic polyurethanes have attracted increasing attention as advanced shape memory materials. Using the prepolymer method, novel fast-responding shape memory thermoplastic polyurethanes (SMTPUs) were prepared from 100% bio-based polyester polyol, poly-propylene succinate derived from corn oil, diphenyl methane diisocyanate, and bio-based 1,3-propanediol as a chain extender. The morphologies of the SMTPUs were investigated by Fourier transform infrared spectroscopy, atomic force microscopy, and X-ray diffraction, which revealed the interdomain spacing between the hard and soft phases, the degree of phase separation, and the intermixing level between the hard and soft phases. The thermal and mechanical properties of the SMTPUs were also investigated, wherein a high hard segment content imparted unique properties that rendered the SMTPUs suitable for shape memory applications at varying temperatures. More specifically, the SMTPUs exhibited a high level of elastic elongation and good mechanical strength. Following compositional optimization, a tensile strength of 24–27 MPa was achieved, in addition to an elongation at break of 358–552% and a hardness of 84–92 Shore A. Moreover, the bio-based SMTPU exhibited a shape recovery of 100%, thereby indicating its potential for use as an advanced temperature-dependent shape memory material with an excellent shape recoverability.

This study developed bio-based waterborne polyurethane (BWPU) dispersions containing lignin as a sustainable filler with castor oil (CO), polycaprolactone diol (PCL), or poly(trimethylene ether) glycol (PO3G). The effects of the polyol structure and the presence of lignin on the mechanical performance, thermal stability, water absorption, ethanol resistance, and UV-blocking capabilities of the resulting BWPU samples were evaluated. The results revealed that lignin affects the molecular packing and interchain interactions of CO-based BWPU, thus improving its tensile strength and thermal stability while reducing its water absorption and ethanol permeability. In the PCL-based BWPU, lignin had a minimal impact on water absorption and ethanol resistance but led to greater UV-blocking ability due to interactions between the semi-crystalline matrix of PCL and the aromatic structure of the lignin. In the PO3G-based BWPU, lignin disrupted the polymer network, increasing its water absorption and reducing its ethanol resistance but significantly improving its elongation and UV-shielding behavior. These results highlight the dual role of lignin as a sustainable reinforcing agent and functional additive in enhancing the properties of BWPU. By tailoring the polyol structure and optimizing lignin use, this study demonstrates a framework for the development of eco-friendly PU composites suitable for use as coatings, barriers, UV-shielding films, and packaging

Cellulose nanofibril (CNF)-based hydrogels, owing to their sustainability, biocompatibility, and versatile mechanical properties, are promising for biomedical applications. This review analyzes the recent advances and biomedical applications of CNF hydrogels. CNF hydrogels can be prepared via physical and chemical crosslinking. Physical crosslinking involves surface charge density control, pH manipulation, and flow-based processing to generate stable networks, whereas chemical crosslinking employs agents such as epichlorohydrin and citric acid to form permanent covalent bonds. These approaches enable precise control over hydrogel properties, including mechanical strength, porosity, and stimuli responsiveness. CNF hydrogels are particularly promising in drug delivery systems and tissue engineering. CNFs as drug delivery vehicles offer enhanced bioavailability and drug loading capacity owing to their open pore structure and large surface area. Recent developments in stimuli-responsive and injectable CNF hydrogels have enabled controlled drug release and improved targeting capabilities. Moreover, CNF hydrogels serve as effective scaffolds for cell growth and tissue regeneration, with applications in cartilage engineering and wound healing. Integrating CNF hydrogels with 3D bioprinting technology has generated complex tissue structures. However, several challenges remain, including the need for the standardization of toxicology assessments, optimization of large-scale production processes, and development of sophisticated control mechanisms for drug delivery. Future research should advance manufacturing technologies, improve long-term stability, and develop standardized testing protocols for regulatory compliance.

The mechanical and thermal conductivity properties of two composite elastomers were studied. Styrene–butadiene rubber (SBR) filled with functionalized graphene oxide (GO) and silica nanofibers, and styrene–butadiene–styrene (SBS) block copolymers filled with graphene oxide. For the SBR composites, GO fillers with two different surface functionalities were synthesized (cysteamine and dodecylamine) and dispersed in the SBR using mechanical and liquid mixing techniques. The hydrophilic cysteamine-based GO fillers were dispersed in the SBR by mechanical mixing, whereas the hydrophobic dodecylamine-based GO fillers were dispersed in the SBR by liquid mixing. Silica nanofibers (SnFs) were fabricated by electrospinning a sol–gel precursor solution. The surface chemistry of the functionalized fillers was studied in detail. The properties of the composites and the synergistic improvements between the GO and SnFs are presented. For the SBS composites, GO fillers were dispersed in the SBS elastomer at several weight percent loadings using liquid mixing. Characterization of the filler material and the composite elastomers was performed using x-ray photoelectron spectroscopy, x-ray diffraction, transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, dynamic mechanical analysis, tensile testing, nanoindentation, thermal conductivity and abrasion testing.