Poly(ester-carbonate) copolymers were synthesized through triethylborane (TEB)-activated, one-pot copolymerization of epoxides with anhydrides (AH) and CO₂. Depending upon the feeding ratio of AH to the epoxides, poly(ester-carbonate) copolymers with random and tapered ester structures could be derived due to the much higher reactivity of AH toward growing oxanions compared to the reactivity of CO₂. Anhydrides like succinic anhydride (SA) and phthalic anhydride (PA) when tried in terpolymerization with epoxides, like propylene oxide (PO) and cyclohexene oxide (CHO), and CO₂ indeed exhibited such high reactivities in comparison to CO₂ that tapered block structures were eventually obtained for high feeding ratios of AH to PO and random copolymers for the AH-to-epoxide feeding ratio lower than 10%. Terpolymerization with different feeding ratios of anhydrides to epoxides was thus systematically investigated. In an alternate path, diblock poly(ester-b-carbonate)s were prepared by sequential copolymerization of epoxide/anhydride and epoxide/CO₂. All of the obtained copolymers were characterized by ¹H nuclear magnetic resonance (NMR), diffusion-ordered spectroscopy (DOSY), gel permeation chromatography (GPC), and differential scanning calorimetry (DSC). The structures and properties of copolymers obtained by terpolymerizations and block copolymerizations were compared.

A manganese–salen complex is shown to be effective in catalyzing the dehydrogenative coupling of hydroxyl groups with hydrosilane.

Poly(silylether)s are interesting materials because of their degradation property under hydrolytic conditions and have been prepared via hydrosilylation polymerization from dicarbonyl and hydrosilanes, and via dehydrogenative cross-coupling of diols and hydrosilanes under catalytic conditions. Here, we present a manganese–salen compound based on an inexpensive and nontoxic metal that could effectively catalyze both polymerization reactions with hydrosilane. A series of poly(silylether)s containing various aliphatic and aromatic backbones have been synthesized from diol and dicarbonyl substrates. Moderate to high yields of polymers with number-average molecular weights up to 15 kg/mol are obtained. Because of the dual activity of the manganese catalyst, unsymmetrical substrates with mixed functional groups, such as p-hydroxybenzaldehyde, p-hydroxy benzylalcohol, and 3-(4-hydroxyphenyl)-1-propanol, have been employed to afford poly(silylether)s with multiple silicon connectivity in the main chain.