This paper reports on the use of low-damage atomic layer etching (ALE) performed using O₂ and BCl₃ plasma for etching (Al)GaN. The proposed ALE process led to excellent self-limiting etch characteristics with a low direct current (DC) self-bias, which resulted in a high linearity between the etching depth and number of cycles. The etching damage was evaluated using several methods, including atomic force microscopy, photoluminescence (PL), and X-ray photoelectron spectroscopy, and the I–V properties of the recessed Schottky diodes were compared with those of digital etching performed using O₂ plasma and HCl solution. The electrical characteristics of the recessed Schottky diode fabricated using the proposed ALE process were superior to those of the diodes fabricated using the conventional digital etching process. Moreover, the ALE process yielded a higher PL intensity and N/(Al + Ga) ratio of the etched AlGaN surface, along with a smoother etched surface.

This study investigated the effects of a thin aluminum oxynitride (AlO_xN_y) gate insulator on the electrical characteristics of AlGaN/GaN-on-SiC metal-insulator-semiconductor high electron mobility transistors (MIS-HEMTs). The fabricated AlGaN/GaN-on-SiC MIS-HEMTs exhibited a significant reduction in gate leakage and off-state drain currents in comparison with the conventional Schottky-gate HEMTs, thus enhancing the breakdown voltage. The effects of gate recess were also investigated while using recessed MIS-HEMT configuration. The Johnson’s figures of merit (= f_T × BV_gd) for the fabricated MIS-HEMTs were found to be in the range of 5.57 to 10.76 THz·V, which is the state-of-the-art values for GaN-based HEMTs without a field plate. Various characterization methods were used to investigate the quality of the MIS and the recessed MIS interface.

We optimized a silicon nitride (SiN_x) passivation process using a catalytic-chemical vapor deposition (Cat-CVD) system to suppress the current collapse phenomenon of AlGaN/GaN-on-Si high electron mobility transistors (HEMTs). The optimized Cat-CVD SiN_x film exhibited a high film density of 2.7 g/cm³ with a low wet etch rate (buffered oxide etchant (BOE) 10:1) of 2 nm/min and a breakdown field of 8.2 MV/cm. The AlGaN/GaN-on-Si HEMT fabricated by the optimized Cat-CVD SiN_x passivation process, which had a gate length of 1.5 μm and a source-to-drain distance of 6 μm, exhibited the maximum drain current density of 670 mA/mm and the maximum transconductance of 162 mS/mm with negligible hysteresis. We found that the optimized SiN_x film had positive charges, which were responsible for suppressing the current collapse phenomenon.