This paper explores the photochemical synthesis of noble metal nanoparticles, specifically gold (Au) and silver (Ag) nanoparticles, using a one-component photoinitiator system. The synthesis process involves visible light irradiation at a wavelength of 419 nm and an intensity of 250 mW/cm². The radical-generating capabilities of the photoinitiators were evaluated using electron spin resonance (ESR) spectroscopy. The main objective of this study was to investigate how the concentration of metal salts influences the size and distribution of the nanoparticles. Proposed mechanisms for the photochemical formation of nanoparticles through photoinitiated radicals were validated using cyclic voltammetry. The results showed that the concentration of AgNO₃ significantly impacted the size of silver nanoparticles, with diameters ranging from 1 to 5 nm at 1 wt% and 3 wt% concentrations, while increasing the concentration to 5 wt% led to an increase in the diameter of silver nanoparticles to 16 nm. When HAuCl₄ was used instead of AgNO₃, it was found that the average diameters of gold nanoparticles synthesized using both photoinitiators at different concentrations ranged between 1 and 4 nm. The findings suggest that variations in HAuCl₄ concentration have minimal impact on the size of gold nanoparticles. The photoproduction of AuNPs was shown to be thermodynamically favorable, with the reduction of HAuCl₄ to Au⁰ having ∆G values of approximately −3.51 and −2.96 eV for photoinitiators A and B, respectively. Furthermore, the photoreduction of Ag⁺¹ to Ag⁰ was demonstrated to be thermodynamically feasible, with ∆G values of approximately −3.459 and −2.91 eV for photoinitiators A and B, respectively, confirming the effectiveness of the new photoinitiators on the production of nanoparticles. The synthesis of nanoparticles was monitored using UV-vis absorption spectroscopy, and their sizes were determined through particle size analysis of transmission electron microscopy (TEM) images.

The copper II complex (HLCuCl) carrying 2,4 dinitrophenylhydrazone (L) is synthesized and evaluated as a new photoredox catalyst/photoinitiator in combination with triethylamine (TEA) and iodonium salt (Iod) for the radical polymerization of ethylene glycol diacrylate during exposure to visible light using a photoreactor at 419 nm. The copper complex reactivity with TEA/Iod salt/gold chloride showed a good production and stability of gold nanoparticles. Finally, the high performance of Cu (II) complex for radical photopolymerization incorporating gold nanoparticles is provided. The photochemical mechanisms for the production of initiating radicals are studied using cyclic voltammetry. Polymer nanocomposites containing gold nanoparticles (Au NPs) in situ photogenerated during the irradiation process were prepared. The formation of Au NPs inside the polymer matrix was through UV–Vis and EDS/SEM analyses.

Benzophenone derivatives were evaluated as new photoinitiators in combination with triethylamine (TEA) and iodonium salt (Iod) for very rapid and efficient formation of metal nanoparticles in an organic solvent, by which silver and gold ions were reduced under light at 419 nm (photoreactor) with an irradiation intensity of 250 microwatts/cm². The new benzophenone derivatives combined with TEA/Iod salt showed good production of metal nanoparticles (Au⁰ and Ag⁰) and a small size of nanoparticles of around 4-13 nm. The photochemical mechanisms for the production of initiating radicals were studied using cyclic voltammetry, where a negative ΔG of around -1.96 eV was obtained, which made the process favorable. The obtained results proved the formation of amine and phenyl radicals, which led to the reduction of gold III chloride or silver ions to the gold and silver NPs. The UV-vis spectroscopy technique was used as a very beneficial tool for the surface plasmon resonance band detection of metal nanoparticles. To sum up the results, we have observed that nanoparticles (NPs) were distributed differently in different photoinitiator systems and the particle size also changed by changing the system of initiation. In comparison to the system alone, not only were the nanoparticles smaller but they were also generated within a shorter period of irradiation time for the system BP\Iod\TEA. Finally, the quenching process of benzophenone fluorescence by the gold and silver nanoparticles was investigated.

In this study, we developed highly efficient nonwoven membranes by modifying the surface of polypropylene (PP) and poly(butylene terephthalate) (PBT) through photo-grafting polymerization. The nonwoven membrane surfaces of PP and PBT were grafted with poly(ethylene glycol) diacrylate (PEGDA) in the presence of benzophenone (BP) and metal salt. We immobilized tertiary amine groups as BP synergists on commercial nonwoven membranes to improve PP and PBT surfaces. In situ Ag, Au, and Au/Ag nanoparticle formation enhances the nonwoven membrane surface. SEM, FTIR, and EDX were used to analyze the surface. We evaluated modified nonwoven membranes for photocatalytic activity by degrading methylene blue (MB) under LED and sunlight. Additionally, we also tested modified membranes for antibacterial activity against E. coli. The results indicated that the modified membranes exhibited superior efficiency in removing MB from water. The PBT showed the highest efficiency in dye removal, and bimetallic nanoparticles were more effective than monometallic. Modified membranes exposed to sunlight had higher efficiency than those exposed to LED light, with the PBT/Au/Ag membrane showing the highest dye removal at 97% within 90 min. The modified membranes showed reuse potential, with dye removal efficiency decreasing from 97% in the first cycle to 85% in the fifth cycle.

The copper II complex’s novel benzimidazole Schiff base ligands were manufactured and gauged as a new photoredox catalyst/photoinitiator amalgamated with triethylamine (TEA) and iodonium salt (Iod) for the polymerization of ethylene glycol diacrylate while exposed to visible light by an LED Lamp at 405 nm with an intensity of 543 mW/cm² at 28 °C. Gold and silver nanoparticles were obtained through the reactivity of the copper II complexes with amine/Iod salt. The size of NPs was around 1–30 nm. Lastly, the high performance of copper II complexes for photopolymerization containing nanoparticles is presented and examined. Ultimately, the photochemical mechanisms were observed using cyclic voltammetry. The preparation of the polymer nanocomposite nanoparticles in situ was photogenerated during the irradiation LED at 405 nm with an intensity of 543 mW/cm² at 28 °C process. UV-Vis, FTIR, and TEM analyses were utilized for the determination of the generation of AuNPs and AgNPs which resided within the polymer matrix.